Colorant compounds containing copolymerizable vinyl groups

ABSTRACT

Disclosed are novel colorant compounds which contain one or more ethylenically-unsaturated (vinyl), photopolymerizable radicals which may be copolymewrized (or cured) with ethylenically-unsaturated monomers to produce colored compositions such as colored acrylic coatings and polymers, e.g., coatings and polymers produced from acrylate and methacrylate esters, colored polystyrenes, and similar colored polymeric materials derived from other ethylenically-unsaturated monomers. The present invention also pertains to processes for the preparation of certain of the photopolymerizable colorant compounds.

CROSS REFERENCE TO RELATED APPLICATION

This application is a DIV of Ser. No. 09/920,904 filed Aug. 02, 2001, now U.S. Pat. No 6,727,372, which is claims the benefit of U.S. Provisional Application Ser. No. 60/223,521, filed Aug. 7, 2000.

FIELD OF THE INVENTION

This invention pertains to certain novel colorant compounds which contain one or more ethylenically-unsaturated (vinyl), photopolymerizable radicals which may be copolymerized (or cured) with ethylenically-unsaturated monomers to produce colored compositions such as colored acrylic polymers, e.g., polymers produced from acrylate and methacrylate esters, colored polystyrenes, and similar colored polymeric materials derived from other ethylenically-unsaturated monomers. The present invention also pertains to processes for preparing certain of the photopolymerizable colorant compounds.

BACKGROUND AND PRIOR ART

It is known (J.S.D.C., April 1977, pp 114–125) to produce colored polymeric materials by combining a reactive polymer such terepolymers having epoxy groups or polyacryloyl chloride with anthraquinone dyes containing nucleophilic reactive groups such as amino or hydroxy groups; to graft acryloylaminoanthraquinone dyes to the backbone of vinyl or divinyl polymers; and to polymerize anthraquinone dyes containing certain olefinic groups to produce polymeric dyes/pigments. U.S. Pat. No. 4,115,056 describes the preparation of blue, substituted 1,4-diaminoanthraquinone dyes containing one acryloyloxy group and and the use of the dyes in coloring various fibers, especially polyamide fibers. U.S. Pat. No. 4,943,617 discloses liquid crystalline copolymers containing certain blue, substituted 1,5-diamino-4,8-dihydroxyanthraquinone dyes containing an olefinic group copolymerized therein to provide liquid crystal copolymers having high dichromism. U.S. Pat. No. 5,055,602 describes the preparation of certain substituted 1,4-diaminoanthraquinone dyes containing polymerizable acryloyl and methacryloyl groups and their use in coloring polyacrylate contact lens materials by copolymerizing.

U.S. Pat. No. 5,362,812 discloses the conversion of a variety of dye classes, including anthraquinones, into polymeric dyes by (a) polymerizing 2-alkenylazlactones and reacting the polymer with dyes containing nucleophilic groups and by (b) reacting a nucleophilic dye with an alkenylazlactone and then polymerizing the free radically polymerizable dyes thus produced. The polymeric dyes are reported to be useful for photoresist systems and for colorproofing. U.S. Pat. No. 5,367,039 discloses a process for preparing colored vinyl polymers suitable for inks, paints, toners and the like by emulsion polymerization of a vinyl monomer with reactive anthraquinone dyes prepared by functionalizing certain anthraquinone dyes with methacryloyl groups.

The preparation of a variety of dyes, including some anthraquinones, which contain photopolymerizable groups and their use for color filters suitable for use in liquid crystal television sets, color copying machines, photosensitive resist resin compositions, and the like are described in U.S. Pat. No. 5,578,419.

BRIEF SUMMARY OF THE INVENTION

The first embodiment of the present invention concerns colorant compounds having Formulas I and II:

wherein

A, is a mono-, di-, tri- or tetravalent chromophore;

X is —R₁—O-Q or the phtopolymerizable group —CH₂—C₆H₄-p-C(R₂)═CH₂;

Y is —R₁—O-Q, —CH₂—C₆H₄-p-C(R₂)═CH₂ or Q;

R is selected from hydrogen, C₁–C₆ alkyl, aryl and C₃–C₈ cycloalkyl;

R₁ is selected from C₂–C₈ alkylene, —(—CH₂CH₂O—)_(m)—CH₂CH₂— and 1,4-cyclohexylenedimethylene;

R₂ is selected from hydrogen and C₁–C₆ alkyl;

n is 1 to 4;

m is 1–3;

Q is a photopolymerizable group selected from an organic radical having the formulae: —COC(R₃)═CH—R₄  Ia —CONHCOC(R₃)═CH—R₄  IIa —CONH—C₁–C₆-alkylene OCOC(R₃)═CH—R₄  IIIa

wherein

R₃ is selected from hydrogen or C₁–C₆ alkyl;

R₄ is selected from hydrogen; C₁–C₆ alkyl; phenyl; phenyl substituted with one or more groups selected from C₁–C₆ alkyl, C₁–C₆ alkoxy, —N(C₁–C₆ alkyl)₂, nitro, cyano, C₂–C₆ alkoxycarbonyl, C₂–C₆ alkanoyloxy and halogen; 1- and 2-naphthyl; 1- and 2-naphthyl substituted with C₁–C₆ alkyl or C₁–C₆ alkoxy; 2- and 3-thienyl; 2- and 3-thienyl substituted with C₁–C₆ alkyl or halogen; 2- and 3-furyl; and 2- and 3-furyl substituted with C₁–C₆ alkyl;

R₅ and R₆ are independently selected from hydrogen, C₁–C₆ alkyl, substituted C₁–C₆ alkyl; aryl; or R₅ and R₆ may be combined to represent a —(—CH₂—)₃₋₅— radical;

R₇ is selected from hydrogen or a group selected from C₁–C₆ alkyl, substituted C₁–C₆ alkyl, C₃–C₈ alkenyl, C₃–C₈ cycloalkyl and aryl; and

R₈ is selected from hydrogen, C₁–C₆ alkyl and aryl.

The colorant compounds have good color strength, good solubility in the reactive monomers and good light-fastness. Certain of the colorant compounds exhibit outstanding thermal stability.

A second embodiment of the present invention concerns a process for preparing photopolymerizable colorants having Formula I, wherein X is a p-vinylbenzyl radical having the formula —CH₂—C₆H₄-p-C(R₂)═CH₂ which comprises reacting colored acidic compounds having the structure:

with the compounds having the structure ClCH₂—C₆H₄-p-C(R₂)═CH₂ in the presence of base, wherein A, R₂ and n are as defined previously.

A third embodiment of the present invention concerns a process for preparing photopolymerization colorants having Formula II, wherein Y is a p-vinylbenzyl radical having the formula —CH₂—C₆H₄-p-C(R₂)═CH₂ which comprises reacting colored acidic compounds having the structure

with 4-chloromethylstyrene compounds having the structure ClCH₂—C₆H₄-p-C(R₂)═CH₂ in the presence of a base, wherein A, R, R₂ and n are defined above.

A fourth embodiment of the invention concerns a process for preparing colored photopolymerizable compounds having Formula I and Formula II, respectively, wherein X and Y are —CH₂CH₂—O-Q or —CH₂CH(CH₃)—O-Q, which comprises the steps of

-   (a) reacting a colored acidic compounds having the structures:

respectively, with at least about n molecular equivalents of ethylene or propylene carbonate for each molecular equivalent of acidic compounds to produce the 2-hydroxyalkyl derivatives of said acidic compounds followed by:

-   (b) reaction of said colored hydroxyalkyl derivatives with about n     molecular equivalents of one or more acylating agents having the     structures     ClCOC(R₃)═CH—R₄ or O[COC(R₃)═CH—R₄]₂,  Ib     O═C═N—COC(R₃)═CH—R₄,  IIb     O═C═N—C₁–C₆ alkylene OCOC(R₃) CH—R₄,  IIIb

wherein A, n, Q, R, R₃, R₄, R₅, R₆, R₈ are defined previously.

A fifth embodiment of the present invention concerns a process for preparing compounds of Structure II, wherein Y is a photopolymerizable group Q which comprises reacting colored acidic compounds having the structure:

with at least about n molecular equivalents of one or more acylating agents Ib through IXb described above wherein A, R, n and Q are defined above.

A sixth embodiment of the present invention pertains to a coating composition comprising (i) one or more polymerizable vinyl compounds, (ii) one or more of the colorant compounds having Formulas I and II described above, and (iii) a photoinitiator. A seventh embodiment of the present invention pertains to a polymeric composition, typically a coating, comprising a polymer of one or more acrylic acid esters, one or more methacrylic acid esters and/or other polymerizable vinyl compounds, having copolymerized therein one or more of the colorant compounds having Formulas I and II described above.

DETAILED DESCRIPTION

In formulas I and II, A represents a mono-, di-, tri- or tetravalent residue of a chromophore, i.e., a colored compound, including residues which in combination with —CO₂X produces a chromophore. Examples of the chromophoric residues which A may represent include anthraquinone, anthrapyridone (3H-dibenz-[f, ij]-isoquinoline-2,7-dione, anthrapyrimidine (7H-dibenz-[f,ij]-isoquinoline-7-one), anthrapyrimidine (7H-benzo[e]-perimidine-7-one), anthrapyrimidone, isothiazoloanthrone, azo, bis-azo, methine, bis-methine, coumarin (2-H-1-benzopyran-2-one), 3-aryl-2,5-dioxypyrroline, 3-aryl-5-dicyanomethylene-2-oxypyrroline, perinone, quinophthalone, phthalocyanine, metal phthalocyanine, nitroarylamine or a 2,5-diarylaminoterephthalic ester chromophore.

The terms “C₁–C₆-alkyl” and “C₁–C₈-alkyl” are used herein to denote a straight- or branched-chain, saturated, aliphatic hydrocarbon radical containing one to six, and one to eight, carbon atoms. The term “substituted C₁–C₆-alkyl” is used to denote a C₁–C₆-alkyl group substituted with one or more groups, preferably one to three groups, selected from the group consisting of hydroxy, halogen, cyano, aryl, aryloxy, arylthio, C₁–C₆ alkylthio, C₃–C₈-cycloalkyl, C₂–C₆-alkanoyloxy and —(—O—R₉—)_(p)—R₁₀ wherein R₉ is selected from the group consisting of C₁–C₆ alkylene, C₁–C₆-alkylene-arylene, cyclohexylene, arylene, C₁–C₆-alkylene-cyclohexylene and C₁–C₆-alkylene-cyclohexylene-C₁–C₆-alkylene, R₁₀ is selected from the group consisting of hydrogen, hydroxy, carboxy, C₂–C₆-alkanoyloxy, C₂–C₆-alkoxycarbonyl, aryl and C₃–C₈-cycloalkyl; and p is 1, 2, or 3.

The terms “C₁–C₆-alkylene”, “C₂–C₄-alkylene” and “C₂–C₈-alkylene” are used to denote straight- or branched-chain, divalent, aliphatic hydrocarbon radicals containing one to six, two to four, and two to eight carbons, respectively. These divalent radicals may be substituted with one to three groups selected from C₁–C₆-alkoxy, C₂–C₆-alkoxycarbonyl, C₂–C₆-alkanoyloxy, hydroxy, aryl and halogen. The term “C₃–C₈-alkenyl” is used to denote an aliphatic hydrocarbon radical containing at least one double bond. The term “C₃–C₈-alkynyl” is used to denote an aliphatic hydrocarbon radical containing at least one triple bond and three to eight carbon atoms. The term “C₃–C₈-cycloalkyl” is used to denote a saturated, carbocyclic, hydrocarbon radical having three to eight carbon optionally substituted with one to three C₁–C₆-alkyl group(s). The term “C₃–C₈-cycloalkylene” is used to denote a divalent, carbocyclic hydrocarbon radical which contains three to eight carbon atoms, preferably five or six carbons.

The term “aryl” as used herein denotes phenyl and phenyl substituted with one to three substituents selected from C₁–C₆-alkyl, substituted C₁–C₆-alkyl, C₁–C₆-alkoxy, halogen, carboxy, cyano, C₂–C₆-alkanoyloxy, C₁–C₆-alkylthio, C₁–C₆-alkylsulfonyl, trifluoromethyl, hydroxy, optionally substituted sulfamoyl, C₂–C₆-alkoxycarbonyl, C₂–C₆-alkanoyl-amino and —O—R₁₁, S—R₁₁, —SO₂—R₁₁, —NHSO₂R₁₁ and —NHCO₂R₁₁, wherein R₁₁ is phenyl or phenyl substituted with one to three groups selected from C₁–C₆-alkyl, C₁–C₆-alkoxy and halogen. The term “arylene” as used herein denotes includes 1,2-, 1,3- and 1,4-phenylene and such divalent radicals substituted with one to three groups selected from C₁–C₆-alkyl, C₁–C₆-alkoxy and halogen.

The term “halogen” is used to include fluorine, chlorine, bromine, and iodine. The term “optionally substituted sulfamoyl” is used to describe the group having the structure —SO₂N(R₁₂)R₁₃, wherein R₁₂ and R₁₃ are independently selected from hydrogen, C₁–C₆-alkyl, substituted C₁–C₆-alkyl, C₃–C₈-alkenyl, C₃–C₈-cycloalkyl, aryl and heteroaryl.

The terms “C₁–C₆-alkoxy”, “C₂–C₆-alkoxycarbonyl”, “C₂–C₆-alkanoyl”, “C₂–C₆-alkanoyloxy” and “C₂–C₆-alkanoylamino” are used to denote radicals corresponding to the structures —OR₁₄, —CO₂ R₁₄, —COR₁₄, —OCOR₁₄ and NHCOR₁₄, respectively, wherein R₁₄ is C₁–C₆-alkyl or substituted C₁–C₆-alkyl. The term “heteroaryl” as used herein denotes a 5- or 6-membered aromatic ring containing one to three hetero atom selected from oxygen, sulfur and nitrogen. Examples of such heteroaryl groups are thienyl, furyl, pyrrolyl, imidazolyl, pyrazolyl, thiazolyl, isothiazolyl, oxazolyl, isoxazolyl, triazolyl, thiadiazolyl, oxadiazolyl, tetrazolyl, pyridyl, pyrimidyl, benzoxazolyl, benothiazolyl, benzimidazolyl, indolyl and the like and these optionally substituted with one to three groups selected from C₁–C₆-alkyl, C₁–C₆-alkoxy, substituted C₁–C₆-alkyl, halogen, C₁–C₆-alkylthio, aryl, arylthio, aryloxy, C₂–C₆-alkoxycarbonyl and C₂–C₆-alkanoylamino.

The preferred azo dyes of the invention encompassed by Formula I have the following general Formula XIII: D-N═N-Z  XIII wherein D is the residue of an aromatic or heteroaromatic, diazotizable amine which has been diazotized and coupled with an electron rich coupling component H-Z and is preferably derived from the aromatic and heteroaromatic classes of unsubstituted and substituted anilines, 1-naphthylamines, 1-aminoanthraquinones, 4-aminoazobenzenes, 2-aminothiazoles, 2-aminobenzothiazoles, 3-amino-2,1-benzisothiazoles, 2-aminothieno [2,3-d]thiazoles, 5-aminopyrazoles, 4-aminopyrazoloiso-thiazoles, 2-amino-1,3,4-thiadiazoles, 5-amino-1,2,3-thiadiazoles, 5-amino-1,2,3-triazoles, 2-amino-1,3,4-triazoles, 2(5) aminoimidazoles, 3-aminopyridines, 2(3)aminothiophenes, 2(3)aminobenzo [5]thiophenes, 2-aminothieno[3,2-5]thiophenes, 3-aminothieno[2,3]-isothiazoles, 3-amino-7-benz-2,1-isothiazoles, 3-aminoisothiazolo[3,4-d]pyridines, 3(4)-aminophthalimides and 5(6) amino-1,2-benzisothiazolon-1,1-dioxides; wherein the substituuents which are present on D are selected from C₁–C₆-alkyl; C₁–C₆-alkoxy; C₃–C₈-cycloalkyl; halogen; C₂–C₆-alkoxycarbonyl;

C₂–C₆-alkanoyloxy; formyl; C₂–C₆-alkanoyl; dicyanovinyl; thiocyano; trifluoromethyl; trifluoroacetyl; cyano; carbamoyl; —CONHC₁–C₆-alkyl; —CON(C₁–C₆-alkyl)₂; —CONH aryl; sulfamoyl; —SO₂NHC₁–C₆-alkyl; —SO₂N(C₁–C₆-alkyl)₂; —SO₂NHaryl; —SO₂NHC₃–C₈-cycloalkyl; —CONHC₃–C₈-cycloalkyl; aryl; aroyl; heteroaryl; NHSO2C₁–C₆ alkyl; N(C₀–C₆-alkyl) SO₂C₁–C₆-alkyl; NHSO₂ aryl; NHCO₂C₁–C₆-alkyl; NHCONH C₁–C₆-alkyl; NHCONH aryl; —N-(C₁–C₆-alkyl)-aryl; arylazo; aryloxy; arylthio; C₃–C₈-cycloalkoxy; heteroarylazo; heteroarylthio; arylsulfonyl; tricyanovinyl; aryloxysulfonyl; C₁–C₆-alkylsulfonyl; fluorosulfonyl; trifluoromethylsulfonyl; hydroxy; nitro and —CH=AM wherein AM is the residue of an active methylene compound; —CO₂X and

wherein -L- is a linking group selected from —O—, —S— and —SO₂— and X is as defined previously; Z is the residue of an electron rich coupling component selected from the classes of anilines, 1,2,3,4-tetrahydro-quinolines, aminonaphthylamines, benzomorpholines (3,4-dihydro-2H-1,4-benzoxazines), pyrazolones, pyrazoles, 3-cyano-6-hydroxy-2-pyridones, 2,3-dihydroindoles, indoles, 4-hydroxycoumarins, 4-hydroxy-2-quinolones, imidazo[2,1-b]-thiazoles, 2,6-diamino-3-cyanopyridines; 5,5-dimethyl-1,3-cyclohexanedione (dimedone), phenols, naphthols and 2,4-pentanediones; wherein the azo compounds of Formula XIII contain a total of from one to four photopolymerizable groups (—CO₂X), wherein said group(s) may be positioned on moiety D and/or moiety Z.

Another group of preferred azo dye of the invention encompassed by Formula II have the general Formula XIV: D₁-N═N-Z₁  XIV wherein D₁ is the residue of an aromatic or hereroaromatic amine which has been diazotized and coupled with an electron rich coupling component HZ₁, wherein D₁ is derived from the same optionally substituted aromatic amines and heteroaromanic amines as described for Formula XIII above, except that the photopolymerizable group which may be present on D₁, is a triazolyl radical having the formula:

and wherein R and Y are as previously defined; Z₁ is the residue of a coupling component selected from the same classes as described above for Z in Formula XIII and which may be substituted with the group

with the provision that the azo compounds of Formula XIV contain a total of from one to four photopolymerizable groups

wherein said groups(s) may be positioned on moiety D₁ and/or moiety Z₁.

Typical coupler residues represented by Z above in Formula XIII include the groups having the structures:

wherein R₁₅ is hydrogen or 1–2 groups selected from C₁–C₆-alkyl, C₁–C₆-alkoxy, halogen, NHCOR₂₂, NHCO₂R₂₂, NHCON(R₂₂) R₂₃ and NHSO₂R₂₃, wherein R₂₂ is selected from hydrogen, C₁–C₆-alkyl, C₃–C₈-cycloalkyl and aryl, R₂₃ is selected from C₁–C₅-alkyl, C₃–C₈-cycloalkyl and aryl, wherein each C₁–C₆ alkyl group in R₂₂ and R₂₃ may be further substituted with one or more groups selected from C₁–C₆-alkoxy, hydroxy, C₃–C₈-cycloalkyl, aryl, aryloxy, arylthio, cyano, succinimido, —CO₂X,

wherein —CO₂X is a photopolymerizable group as described above; L₁ is selected from a covalent bond, —O—, —S—, —SO₂—, —CO₂—, —SO₂NH—, —CONH— and —SO₂N(C₁–C₆-alkyl)—; wherein each aryl group in R₂₂ and R₂₃ in the definition of R₁₅ may be substituted with at least one photopolymerizable —CO₂X group; wherein R₂₄ represents hydrogen or 1–2 groups selected from —CO₂X, C₁–C₆-alkyl, C₁–C₆-alkoxy and halogen; R₁₆ and R₁₇ are independently selected from hydrogen; C₃–C₈-cycloalkyl; C₃–C₈-alkenyl; C₃–C₈-alkynyl; C₁–C₆-alkyl and C₁–C₆-alkyl substituted with one or more groups selected from —CO₂X,

C₃–C₈-cycloalkyl, aryl, hydroxy, cyano, —OC₂H₄OH, —SCH₂CH₂OH, halogen, —OC₁–C₆-alkyl, —S C₁–C₆-alkyl, —O aryl, —S aryl, —SO₂ aryl, —SO₂C₁–C₆—S heteroaryl, 2-pyrrolidino, phthalimidino, phthalimdo, succinimido, glutarimido, o-benzoic sulfimido, —NHCOC₁–C₆-alkyl, —NHCOH, —NHSO₂ C₁–C₆-alkyl, —NHSO₂aryl, —NHCOaryl, —NHCO₂C₁–C₆-alkyl, —SO₂NH₂, —CONH₂, —SO₂NH—C₁–C₆-alkyl, —SO₂N(C₁–C₆-alkyl)₂, —CO₂C₁–C₆-alkyl, —CONH C₁₋C₆-alkyl, —CO₂-aryl, —CON—(C₁–C₆-alkyl)₂, —CONH-aryl, —CON—(C₁–C₆-alkyl)aryl, —SO₂N(C₁–C₆-alkyl)aryl, —OCOC₁–C₆-alkyl, —OCOaryl, —OCO₂C₁–C₆-alkyl; groups of the formulae:

wherein Y₂ is selected from 1,2-phenylene; 1,2-phenylene substituted with C₁–C₆alkyl, C₁–C₆-alkoxy, halogen, CO₂C₁–C₆-alkyl or nitro; C₂–C₄ alkylene; —OCH₂—; —SCH₂—; —CH₂OCH₂—; —CH₂SCH₂—; —NHCH₂—; —NHCH₂CH₂—N(C₁-C₆-alkyl)CH₂—; —N(C₁–C₆-alkyl)CH₂CH₂; —NHC(aryl)₂, and wherein R₁₆ and R₁₇ may be combined with themselves or another element to which they are attached to form a radical Z having the formula:

wherein L₃ is selected from a covalent bond, —O—, —S—, —CH₂—, —SO₂—, —N(COC₁–C₆-alkyl)-, —N(SO₂C₁–C₆-alkyl)-, —N(COaryl)- and —N(SO₂aryl)-; R₁₈, R₁₉ and R₂₀ are independently selected from hydrogen and C₁–C₆-alkyl; R₂₁ is selected from hydrogen, C₁–C₆-alkyl and aryl.

Typical coupler residue represented by Z₁ is Formula XIV include those mentioned immediately above Z except that the photopolymerizable group which may be present as a substituent or on R₁₅, R₁₆, R₁₇, R₂₂, or R₂₃ is the triazolyl group having the formula:

instead of those listed.

The preferred methine, bis-methine, 3-aryl-2,5-dioxypyrroline, 3-aryl-5-dicyanomethylene-2-oxypyrroline and coumarin compounds of Formula I have the following general Formulas XV, XVI, XVII, XVIII and XIX respectively;

wherein R₂₅ is an electron rich aromatic residue selected from the following:

wherein R₁₆, R₁₇, R₁₈, R₁₉, R₂₀ and R₂₁ are as defined for Z previously in Formula XIII; wherein R₁₆′ is selected from the same groups as R₁₆; wherein R₂₆ is selected from cyano, C₁–C₆-alkoxycarbonyl, C₁–C₆-alkylsulfonyl, arylsulfonyl, aryl, heteroaryl, formyl, C₁–C₆-alkanoyl or —CH=AM; wherein R₂₇ is hydrogen or cyano; wherein AM is the residue of an active methylene compound selected from malononitrile, α-cyanoaceticacid esters, malonic acid esters, α-cyanoacetic acid amides, α-C₁–C₆-alkylsulfonyl-acetonitriles, α-arylsulfonylacetonitriles, α-C₁–C₆-alkanoylacetonitriles, α-arylsulfonyl-acetonitriles, α-C₁–C₆-alkanoylacetonitriles, α-arylacetonitriles, α-herero-acylacetonitriles, bis(heteroaryl) methanes, 1,3-indanediones, 2-furanones, benzo-2-furanones, benzo (b) thieno-3-xlidene propanedinitrile-5,5-dioxides, 1,3-bis(dicyanomethylene)indanes, barbituric acid, 5-pyrazolones, dimedone, 3-oxo-2,3-dihydro-1-benzothiophene-1,1-dioxides, aryl C(CH₃)═C(CN)₂ and NC CH₂ CO₂X, R₂₈; wherein —CO₂X is a photopolymerizable group as previouly defined.

Examples of the anthraquinone (Formulas XX a–e), anthrapyridone (3H-dibenz-[f,ij]-isoquinoline-2-7-dione) (Formulas XXI a–e) and anthrapyridine (7H-dibenz-[f, ij]-isoquinoline-7-one) (Formulas XXII a–e) colorants include the compounds having the structures set forth below:

wherein R₂₈ is hydrogen or represents 1–4 groups selected from amino; C₁–C₈-alkylamino; C₁–C₈-alkylamino substituted with one 1 or more groups selected from hydroxy, cyano, halogen, aryl, heteroaryl, C₃–C₈-cycloalkyl, furyl, C₁–C₆-alkoxy, C₁–C₆-alkylthio, arylthio, aryloxy, —(OCH₂CH₂—)₁₋₃OR′, wherein R′ is selected from hydrogen, C₁–C₆-alkyl and C₂–C₆-alkanoyloxy; C₃–C₈-cycloalkylamino; C₃–C₈-alkenylamino; C₃–C₈-alkynylamino; arylamino; furfurylamino; C₁–C₆-alkoxy; —(OCH₂CH₂—)₁₋₃OR′, wherein R′ is as defined previously; halogen; hydroxy; C₁–C₆-alkylthio; arylthio; aryl; aryloxy; arylsulfonyl C₂–C₆-alkanoyl; aroyl; C₂–C₆-alkanoyloxy; C₂–C₆-alkoxycarbonyl; heteroaryl; heteroarylthio; cyano; nitro; trifluoromethyl; thiocyano; —SO₂C₁–C₆-alkyl; —SO₂NH₂; —SO₂NHC₁–C₆-alkyl; —SO₂N(C₁–C₆alkyl)₂; —SO₂N(C₁–C₆alkyl)aryl; —SO₂NHaryl; —CONH₂; CONHC₁–C₆-alkyl; —CON(C₁–C₆-alkyl)₂; —CONHaryl; —CON(C₁–C₆-alkyl)aryl; C₁–C₆-alkyl; tetrahydrofurfurylamino; 4-(hydroxymethyl)cyclohexylmethylamino; and

R₂₉ is hydrogen or 1–2 groups selected from C₁–C₆-alkyl, halogen and C₁–C₆-alkoxy; R₃₀ is selected from hydrogen, C₁–C⁸-alkyl, substituted C₁–C₈-alkyl as defined previously in the definition of R₂₈, aryl and C₃–C₈-cycloalkyl; R₃₁ is selected from hydrogen, cyano, C₁–C₆-alkoxy, C₁–C₆-alkylthio, aryl, aryloxy, arylamino, arylthio, heteroaryl, heteroarylthio, halogen, C₂–C₆-alkoxycarbonyl, aroyl; C₁–C₆-alkylsulfonyl, arylsulfonyl and C₁–C₆-alkyl-amino; R₃₂ is selected from hydrogen, C₁–C₆-alkyl, aryl and —N(R₃₃)R₃₄, wherein R₃₃ and R₃₄ are independently selected from hydrogen; C₁–C₆-alkyl; C₁–C₆-alkyl substituted with C₂–C₆-alkanoyloxy, aryl and C₃–C₈-cycloalkyl; aryl; C₃–C₈-cycloalkyl; wherein R₃₃ and R₃₄ may be combined to produce divalent radicals such as —(CH₂)—_(4–6) and —CH₂CH₂-L₆—CH₂CH₂—, wherein L₆is selected from —O—, —S—, —SO₂— and —N(R₃₄)—, wherein R₃₄′ is selected from hydrogen, C₁–C₆-alkyl, aryl, aroyl, C₁–C₆— alkanoyl, C₁–C₆-alkylsulfonyl and aryl-sulfonyl; L₄ and L₅ are selected from —O—, —S—, —SO₂—, —CON(R₃₃)— and —SO₂N(R₃₃)—.

Some of the preferred colorants encompassed by Formula I wherein A is a quinophthalone chromophore have the following Formula XXIII:

wherein R₃₅ is selected from hydrogen, bromine, arylthio, heteroarylthio, arylsulfonyl,

wherein X and R₂₄ are as defined above.

Some of the preferred nitroarylamine colorants encompassed by Formula I wherein A is a nitroarylamine chromophore have the following Formula (XXIV):

wherein R₃₆ is selected from hydrogen, halogen, C₁–C₆-alkyl and C₁–C₆-alkoxy; R₃₇ and R₃₈ are independently selected from hydrogen; C₁–C₆-alkyl; C₃–C₆-cycloalkyl; C₃–C₈-cycloalkyl; C₃–C₈-cycloalkyl, C₂–C₆-alkanoyloxy; aryl and

Some of the preferred colorants encompassed by Formula I wherein A is a perinone chromophore correspond to Formulae XXV–XXIX:

wherein R₃₉ is hydrogen or 1–4 groups selected from C₁–C₆-alkyl, C₁–C₆-alkoxy, amino, CO₂X, C₁–C₆-alkylamino, C₃–C₈-cycloalkylamino, arylamino, arylthio, hereroarylthio and

wherein L₇ is selected from —S—, —O— and —NH—, with the provision that one to four —CO₂X groups be present.

Preferred colorants of Formula I containing the 2,5-diarylamino terephthalate chromophore have Formula XXX

wherein R₄₀ is hydrogen or —CO₂X or represents 1–3 groups selected from C₁–C₆-alkyl, C₁–C₆-alkoxy, halogen, and —NHC₂–C₆-alkanoylamino.

The preferred photopolymerizable colorant compounds of the present invention are those of Structures I and II where X and Y, respectively, are selected from —CH₂CH₂OQ, —CH₂CH(CH₃)OQ, —(CH₂CH₂O)₂₋₃—CH₂CH₂OQ, —CH₂C(CH₃)₂CH₂OQ, and —CH₂—C₆H₁₀CH₂OQ and A is an anthraquinone, anthrapyridone or 2,5-diarylaminoterephthalate chromophore residue.

The photopolymerizable colorants having Formula I and II where X and Y are the photopolymerizable p-vinylbenzyl groups radical having the formula —CH₂—C₆H₄-p—C(R₂)═CH₂ are prepared in general by reacting colored acidic compounds having Formulae III and IV with a 4-chloromethylstyreneV, respectively, as follows:

wherein A, n, R and R₂ are as defined previously, to produce colored compounds VI and VII. The reactions of the colored acidic compounds having Formulae III and IV with the 4-chloromethylstyrenes V are carried out in the presence of a polar aprotic solvent such as N,N-dimethylformamide (DMF), N-methyl-2-pyrrolidinone (NMP), N,N-dimethylacetamide (DMAC), sulfolane, etc. in the presence of one or more bases such as an alkali metal carbonate, an alkali metal bicarbonate, a trialkylamine, a cyclic nitrogen compounds such as 1,8-diazabicyclo [5.4.0]undec-7-ene (PBU), 1,5-diazabicyclo [4.3.0]non-5-ene (DBN), and the like. The reaction may under some reaction conditions be facilitated by the presence of a catalytic amount of an alkali metal bromide, alkali metal iodide and/or a conventional phase transfer catalysts, e.g., a tetraalkylammonium halide such as a chloride or bromide. The reactions are usually carried out between about 50° C. to about 150° C., preferably from about 90° C. to about 125° C.

The photopolymerizable dyes having Formulae I and II, where X and Y are —R₁—O-Q are, in general, prepared by first reacting colored acidic acidic compounds having Formulae III and IV with an alkylating agent containing one or more hydroxy groups having Formula VIII as follows:

wherein A, n, R and R₁ are as defined previously and Z is halogen, to produce an intermediate hydroxy compound IX and X. Reaction conditions used for preparing compounds IX and X are those described in the preparation of VI and VII above. Although intermediate hydroxy compounds IX and X where R₁ is —CH₂CH₂— or —CH₂CH(CH₃)— may be prepared as described above by using the corresponding 2-bromo- or chloro-alkanol, the preferred route uses ethylene or propylene carbonate which avoids the use of toxic haloalkanols according to the following equations:

wherein R′ is hydrogen or methyl, to produce hydroxyalkyl derivatives XI and XII. These reactions are facilitated by the presence of catalytic amounts of alkali halides, teraalkylammonium halides or tetraalkylammonium hydroxides. The reactions may be carried out by heating the intermediate colored diacids III and IV with at least molar equivalent amounts of alkylene carbonate. Excess alkylene carbonate also may be useful as the solvent or a co-solvent for the reaction. In particular, ethylene and propylene glycol have been found to be effective co-solvents for the preparation of XI and XII. Compounds IX and X (or XI and XII) are then acylated with one of acylating agents Ib through IXb described above to introduce the desired Q groups to prepare photopolymerizable compounds having Formulae I and II. Q groups Ia–IXa are introduced by reacting hydroxy compounds IX and X with acylating agents Ib–IXb, respectively.

Intermediate colored acidic compounds III and IV are disclosed in U.S. Pat. Nos. 3,689,501; 3,816,392; 4,359,570; 4,403,092; 4,617,373; 4,740,581; 4,745,173; 4,804,719; 4,892,922; 5,030,708; 5,102,980; 5,194,571; 5,274,072; 5,281,659; 5,372,864; 5,962,557 and WO 98/23690, wherein particularly useful diacidic intermediate colorants are disclosed.

The azo dyes above which correspond to Formula XIII and Formula XIV may be prepared by reacting azo dyes containing one to four carboxy groups or one to four 1H-1,2,4-triazol-3-ylthio groups, respectively, to incorporate the photopolymerizable groups as described above. Alternatively, the photopolymerizable groups may be incorporated into the diazotiazable amine and/or coupler portion prior to the synthesis of the azo dyes of Formula XIII and XIV.

Typical aromatic amine coupling components (HZ) which contain photopolymerizable groups and are useful in preparing colorants of Formula XIII have the following structures:

Typical aromatic amine coupling components (HZ₁) which contain copolymerizable groups and are useful in preparing colorants of Formula XIV have the following structures:

In the structures for coupling components HZ and HZ₁, above, R₁₅, R₁₆, R₁₈, R¹⁹, R₂₀, R₂₄, X and Y have the meaning previously ascribed to them.

Colorants of Formula XV, XVII and XVIII which correspond to colorants containing the methine, 3-aryl-2,5-dioxypyrroline and 3-aryl-5-dicyanomethylene-2-oxypyrroline chromophores, respectively, may be prepared by reacting the intermediate aromatic moiety R₂₅H, as defined previously, which contains one or more photopolymerizable groups with either (a) Vilsmeier complex (e.g., from POCl₃/DMF), followed by reaction with the active methylene compound,

to produce colorants of Formula XV, XVII, and XVIII, respectively, wherein R₁₆′ is hydrogen. Compounds of Formula XVII and XVIII, wherein R₁₆ is hydrogen, can be further reacted to introduce photopolymerizable groups if desired.

A third alternative preparative method for azo colorants having Formula XIII and XIV involves the reaction of electron rich coupler precursors containing at least one —CO₂H or 1(H)-1,2,4-triazolyl-3-ylthio group, respectively, with hydroxyalkylating agents to introduce —CO₂—R₁—OH and

groups. These couplers then are reacted with the desired diazonium salts to produce azo dye containing the hydroxy groups which are then reacted further to introduce the photopolymerizable Q groups into the final colorant. Similarly, this method may be employed in the preparation of the colorants having Formulae XV, XVI and XVII by reacting the acidic colored intermediates containing the methine, 3-aryl-2,5-dioxypyrroline or 3-aryl-5-dicyano methylene-2-oxypyrroline chromophores, respectively, to introduce the photopolymerizable group after the chromophore is formed.

As is known to those skilled in the art, the 1(H)-1,2,4-triazolyl moiety of Formula II is a mixture of isomers having the structures:

but that the isomer shown in Formula II probably predominates.

COLORANT EXAMPLES

The copolymerizable dye compounds provided by the present invention and the preparation thereof are further illustrated by the following examples.

Example 1

A mixture of 1,5-bis-(2-carboxyphenylthio) anthraquinone (U.S. Pat. No. 4,359,570, Example 1) (5.13 g, 0.01 mol), potassium carbonate (2.84 g, 0.02 mol) and N,N-dimethylformamide (DMF, 100 mL) was stirred and heated to about 100° C. To the stirred mixture, was added 4-vinylbenzyl chloride (Aldrich, 3.76 g, 0.022 m). Thin-layer chromatography (TLC) using a 50/50 mixture of tetrahydrofuran (THF)/cyclohexane after heating the reaction mixture at about 105° C. for 30 min. showed only one spot with no starting material or mono-reacted product being observed. The reaction mixture was heated for an additional 20 minutes and the yellow dye precipitated by the addition of a mixture of methanol and water. The solid dye was collected by filtration, washed with water and then with a little methanol. The yield of air-dried product was 6.85 g (92% of the theoretical yield). Field desorption mass spectrometry (FDMS) supported the following structure:

An absorption maximum at 447 nm was observed in the UV-visible absorption spectrum in DMF.

Example 2

A mixture of 1,5-bis-(2-carboxyanilino) anthraquinone (U.S. Pat. No. 4,359,570, Example 2) (4.78 g, 0.01 mol), potassium carbonate (2.76 g, 0.02 mol) and DMF (100 mL) was stirred and heated to about 90° C. and 4-vinylbenzyl chloride (Aldrich, 3.76 g, 0.022 mol) was added and heating and stirring continued at about 100° C. for 60 min. TLC (50/50 THF/cyclohexane) showed complete reaction. Methanol (120 mL) was added gradually with stirring to precipitate the red product, which was collected by filtration, washed with water and then dried in air (yield-6.18 g, 87% of the theoretical yield). FDMS supports the following structure:

Example 3

A mixture of 1,5-bis-(isobutylamino)-4,8-bis-(2-carboxyphenylthio) anthraquinone (U.S. Pat. No. 6,197,223, Example 2) (6.54 g, 0.01 mol), potassium carbonate (2.76 g, 0.02 m) and DMF (150 mL) was stirred and heated to about 100° C. To the stirred reaction mixture was added 4-vinylbenzyl chloride (3.76 g, 0.02 mol). The reaction mixture was heated at 95–100° C. for about 60 minutes The reaction mixture was cooled and the gummy product was drowned out by the addition of methanol/water. The liquid was decanted off and the product triturated with methanol. The resulting dark blue solid was collected by filtration, washed with methanol and dried in air (yield-6.95 g, 78% of the theoretical yield). FDMS supported the following structure:

Absorption maxima at 600 nm and 645 nm were observed in the UV-visible absorption spectra in DMF.

Example 4

A mixture of 1,5-bis-(2-carboxyphenylthio)-4,8-bis-(4-tolylthio)-anthraquinone (U.S. Pat. No. 6,197,223) (7.56 g, 0.01 mol), potassium carbonate (K₂CO₃) and DMF (300 mL) was stirred and heated to about 100° C. and then 4-vinylbenzyl chloride (3.84 g, 0.025 mol) was added. The reaction mixture was heated and stirred at about 100° C. for 60 minutes. TLC (50/50 THF/cyclohexanol) showed complete reaction. After cooling, the sticky product was obtained by drowning the reaction mixture with methanol/water. The red product solidified upon standing in contact with methanol and was collected by filtration and dried in air (yield-7.67 g, 78% of the theoretical yield). FDMS supported the following structure:

An absorption maximum was observed at 520 nm in the UV-visible absorption in DMF.

Example 5

A mixture of 1,5-bis-[(1H)-1,2,4-triazol-3 ylthio)]anthraquinone (U.S. Pat. No. 3,689,501) (4.06 g, 0.01 mol), potassium carbonate (2.76 g, 0.02 mol) and DMF (100 mL) was stirred and heated to about 100° C. and 4-vinylbenzyl chloride (3.76 g, 0.022 mol) was added. TLC (50/50 THF/cyclohexane) still showed some mono-substituted product after heating the reaction mixture for 2 hrs. Additional quantities of 4-vinylbenzyl chloride (4.14 g) and potassium chloride (1.38 g) were added and heating continued for another hour to complete the reaction. A gummy yellow solid was produced by drowning the cooled reaction mixture with water. The product was washed by decantation with water and then dissolved in DMF. The DMF solution was drowned gradually into cold water with good stirring and the yellow solid was collected by filtration and dried in air (3.46 g, 54% of the theoretical yield). FDMS supported the following structure:

An absorption maximum at 420 nm was observed in the UV-visible absorption spectrum in DMF.

Example 6a

A mixture of 1,5-bis-(2-carboxyphenylthio) anthraquinone (U.S. Pat. No. 4,359,570, Example 1) (30.6 g, 0.06 mol), ethylene carbonate (88.0 g, 1.0 mol), ethylene glycol (50 mL) and pulverized potassium iodide (5.2 g) was heated and stirred at about 125° C. for about 2.0 hours and then allowed to cool. The reaction mixture was drowned into cold water (150 mL) with stirring. The yellow solid was collected by filtration, washed with warm water and dried in air (yield-35.2 g, 97.8% of the theoretical yield). FDMS supported the following structure:

Example 6b

A mixture of the product of Example 6a (6.0 g, 0.01 mol), DMF (25 mL) and 3-isopropenyl-∝,∝-dimethylbenzyl isocyanate (6 mL, 0.03 mol) was heated and stirred, under nitrogen at about 95–100° C. for about 48 hours. Triethylamine (0.5 mL) was added and heating continued for an additional 48 hours. Water (60 mL) was added portionwise to the hot reaction mixture with stirring. After allowing to cool to room temperature, the yellow product was collected to filtration, washed with water and dried in air. Essentially a quantitative yield of the following product was obtained:

Example 7

The dye of Example 6a above (2.0 g, 3.33 mmol) and toluene (20 mL) were mixed and stirred while most of the toluene was removed under reduced pressure. DMF (50 mL), 4-(dimethylamino)pyridine (DMAP, 82 mg), triethylamine (1.4 mL), hydroquinone (50 mg) and methacrylic anhydride (1.53 g, 9.99 mmol) were added and the reaction mixture stirred at room temperature for 15 hours. The yellow functionalized dye which was precipitated by drowning into water (200 mL) and allowing to stand for several days was collected by filtration, washed with water and 1:1 methanol: water and dried in vacuo. The yield was 2.23 g (91% of the theoretical yield). FDMS supported the following structure:

An absorption maximum at 444 nm was observed in the UV-visible absorption spectrum in DMF.

Example 8a

A mixture of 1,5-bis-(carboxyanilino) anthraquinone (U.S. Pat. No. 4,359,570, Example 2) (59.75 g, 0.125 mol), ethylene carbonate (165 g, 1.875 mol), ethylene glycol (550 mL) and pulverized potassium iodide (11.3 g) was heated at 120–125° C. for 6.5 hours and the mixture allowed to cool. Methanol (400 mL) was added to the stirred reaction mixture. The red solid was collected by filtration, washed with water and dried in air (yield—69.5 g, 98.2% of the theoretical yield). FDMS supported the following structure:

Example 8b

A portion (2.0 g, 3.53 mmol) of the dye of Example 8a above was mixed with toluene (10 mL) and most of the toluene removed under vacuum. DMF (50 mL), DMAP (86 mg), triethylamine (1.5 mL), hydroquinone (20 mg) and methacrylic anhydride (1.63 g, 10.6 mmol) were added and the resulting solution was stirred for 15 hours at room temperature. The reaction mixture was drowned into water (200) and allowed to stand at room temperature for several days. The functionalized red dye was collected by filtration, washed with water and dried in vacuo (yield-2.10 g. 85% of the theoretical yield). FDMS supported the following structure:

An absorption maximum at 525 nm was observed in DMF solution in the UV-visible absorption spectrum.

Example 9

A portion (2.0 g, 3.53 mmol) of the dye from Example 8a above was mixed with toluene and stirred while most of the toluene was removed under reduced pressure. DMF (50 mL), DMAP (86 mg), triethylamine (1.5 mL), hydroquinone (20 mg) and crotonic anhydride (1.63 g, 10.6 mmol) were added and the reaction mixture was stirred for 24 hours. The functionalized red dye was isolated by drowning into water (200 mL), allowing the mixture to stand for a little while and then collecting by filtration. After washing with water the dye was dried in vacuo (yield-2.11 g, 85% of the theoretical yield). FDMS supported the following structure:

An absorption maximum at 522 nm in DMF solution was observed in the UV-visible light absorption spectrum.

Example 10

A mixture of a portion (2.0 g, 3.33 mmol) of the dye of Example 6a above and toluene (10 mL) was stirred and most of the toluene removed under vacuum. DMF (50 mL), DMAP (86 mg) triethylamine (1.4 mL), hydroquinone (20 mg) and crotonic anhydride (7.54 g, 9.99 mmol) were added. The reaction mixture was stirred at room temperature for 24 hours and drowned into water (200 mL) with stirring. The mixture was allowed to stand awhile and the functionalized yellow dye was collected by filtration, washed with water and dried in vacuo (yield 2.01 g, 82% of the theoretical yield). FDMS supported the following structure:

An absorption maximum at 446 nm was observed in DMF in the UV-visible light absorption spectrum.

Example 11a

A mixture of 1-chloroanthraquinone (97.2 g, 0.40 mol), thiosalicylic acid (61.6 g, 0.40 mol), potassium acetate (80 g, 0.80 mol), cuprous chloride (0.5 g) and 2-ethoxyethanol (500 ml) was stirred and heated at reflux (130–135° C.) for 6.5 hours. After allowing to cool, the reaction product was collected by filtration and washing with methanol. The still moist cake was slurried in water (750 ml) and the mixture acidified by the addition of concentrated hydrochloric acid (75 ml). The mixture was stirred at ambient temperature for thirty minutes and the yellow product was collected by filtration, washed with water, washed with a little methanol and dried in air (yield-110.6 g, 76.87% of the theoretical yield). Field desorption mass spectrometry (FDMS) supported the following structure:

Example 11b

A mixture of 1-(2-carboxyphenylthio) arthraquinone (Example 11a) (3.60 g, 0.01 mol), potassium carbonate (1.38 g, 0.01 mol) and N,N-dimethylformamide (DMF), (70 ml) was heated and stirred. At 70° C., 4-vinylbenzyl chloride (1.87 g, 0.011 mol) was added and the reaction mixture was heated to about 100° C. After being heated at about 100° C. for forty minutres, the reaction mixture was allowed to cool and then was drowned with stirring into water (200 ml). After standing overnight at room temperature the yellow solid was collected by filtration, washed with water and dried in air. The yield of product was 4.40 g, 92% of the theoretical yield. FDMS analysis supported the following structure:

An absorption maximum at 425 nm was observed in the UV-visible light absorption spectrum in DMF.

Example 12a

A mixture of thiosalicylic acid (4.63 g, 0.03 mol), potassium carbonate (8.70 g, 0.06 mol) and DMF (75 ml) was heated and stirred at 100° C. for two hours. This mixture was allowed to cool to room temperature and added to a stirred mixture of 1,5-dichloro-4,8-dinitroanthraquinone (5.51 g, 0.015 mol) and DMF (150 ml) which had been cooled to about 0° C. A slight exotherm of 2–3° C. was observed. The mixture was stirred at about 0–5° C. for thirty minutes and then allowed to stand overnight at room temperature. A second mixture of thiosalicylic acid (4.63 g, 0.03 mol), potassium carbonate (8.73 g, 0.06 mol) and DMF (40 ml), which had been stirred for 1.5 hours at room temperature, was added to the previously described mixture. After being heated and stirred at about 100° C. for five hours, the reaction mixture was cooled to room temperature and drowned into water (600 ml) with stirring. After the mixture was acidified by the addition of glacial acetic acid, the dark red product was collected by filtration, washed with water and air dried. (yield-10.70 g, 87.3% of the theorectical yield). FDMS supported the following structure:

Example 12b

A mixture of 1,4,5,8-tetra(2-carboxyphenylthio) anthraquinone (1.22 g, 1.5 mmol) (Example 12a), potassium carbonate (0.83 g, 6.0 mmol) and DMF (20 ml) was stirred and 4-vinylbenzyl chloride (1.01 g, 6.6 mmol) was added. The reaction mixture was heated at about 100° C. for thirty minutes. After cooling to room temperature, the mixture was drowned into methanol. The dark red solid was collected by filtration, washed with methanol and dried in air. The yield of product was 1.58 g, 82% of the theoretical yield. FDMS supported the following structure:

An absorption maximum at 543 nm was observed in the UV-visible light absorption spectrum in DMF solvent.

Example 13a

A mixture of brominated diaminoanthrarufin (3.49 g, 0.01 mol), thiosalicylic acid (3.08 g, 0.02 mol), potassium carbonate (5.53 g, 0.04 mol), cuprous chloride (0.30 g) and DMF (50 ml) was heated at 95–100° C. for about six hours. The reaction mixture was cooled and then drowned into acetone (400 ml). The solid potassium salt of the product was collected by filtration and then redissolved in hot water (300 ml). The free acid was obtained by acidification with glacial acetic acid, collecting by filtration, washing with water and drying in air (yield 3.40 g). FDMS showed the product to be a mixture of mono-and bis-(2-carboxyphenylthio) substituted diaminoanthrarufin having the following structure:

Example 13b

A mixture of a portion of the product from Example 13a (0.85 g), potassium carbonate (0.34 g) and DMF (20 ml) was stirred and heated to about 100° C. and 4-vinylbenzyl chloride (0.38 g) was added. The reaction mixture was stirred at about 100° C. for about thirty minutes, cooled to room temperature and then drowned into methanol (200 ml). The dark blue product was collected by filtration, washed with methanol, water and then again with methanol to promote drying. The air-dried product weighed (0.69 g). FDMS showed the product to have the following structure:

wherein the monosubstitued product was the major predominate structure present. An absorption maximum at 641 nm was observed in the UV-visible light absorption spectrum.

Example 14a

A mixture of 1,8-diamino-2,7-dibromo-4,5-dihydroxyanthraquinone (2.14 g, 0.005 mol), thiosalicylic acid (1.69 g, 0.011 mol), potassium carbonate (3.0 g), cuprous chloride (0.30 g) and DMF (45.0 ml) was heated at steam bath temperature for about 6.0 hours. The reaction mixture was cooled and drowned into acetone (500 ml). The resulting solid was collected by filtration and the acetone-wet material was dissolved in warm water. Acetic acid was added to precipitate the diacid product which was collected by filtration, washed with water and dried in air (yield-2.60 g).

Example 14b

A mixture of 1,8-diamino-4,5-dihydroxy-2,7-bis(carboxyphenylthio) anthraquinone (1.15 g, 2.0 mmol), (from Example 14a) potassium carbonate (0.56 g, 4.0 mmol) and DMF (20 ml) was heated to about 100° C. and 4-vinylbenzyl chloride (0.68 g, 4.4 mml) was added. Stirring and heating were continued at about 100° C. for four hours. The product was isloated by drowning into water and collecting the product by filtration. The product comprises primarily the compound having the following expected structure:

When the product was dissolved in DMF a bright cyan color was obtained.

Example 15

A mixture of 1-cyano-6(3′,5′-dicarboxyphenylamino)-3-methyl-3H-dibenz[f,lj]isoquinoline-2,7-dione (Example 119a of U.S. Pat. No. 6,197,223) (4.65 g, 0.01 mol), potassium carbonate (0.02 mol) and DMF (100 ml) was stirred and heated in about 90° C. and 4-vinylbenzyl chloride (3.73 g 0.022 mol) was added. After being heated at about 110° C. for 3.0 hours, thin-layer chromatography (90/10 THF/cyclohexane) showed the reaction to be complete and the reaction mixture was cooled to room temperature. Methanol (100 ml) was added with stirring to the reaction mixture. After being allowed to stand overnight at room temperature, the product was collected by filtration, washed with methanol and dried in air (yield-3.80 g, 54% of the theoretical yield) and has the structure:

A bright violet color was obtained when the product was dissolved in DMF.

Example 16a

A mixture of 6-bromo-1-cyano-3H-dibenz[f,ij]isoquinoline-2,7-dione (3.65 g, 0.01 mol) thiosalicylic acid (1.54 g, 0.01 mol), potassium carbonate (2.76 g, 0.02 mol) and DMF (60 ml) was stirred and heated at about 95–100° C. for 1.5 hours. After allowing to cool, the reaction mixture was drowned into water (100 ml) and the mixture acidified by the addition of glacial acetic acid. The red solid was collected by filtration, washed with water and dried in air. The yield of product was 4.38 g (100% of the theoretical yield). FDMS supported the following expected structure:

Example 16b

The carboxy anthrapyridone dye of Example 16a (4.38 g, 0.01 mol), potassium carbonate (1.38 g, 0.01 mol) and DMF (100 ml) were stirred together and heated to about 100° C. for 30 minutes. After cooling, water (100 ml) was added dropwise to the stirred reaction mixture. The precipitated red product was collected by filtration, washed with water and dried in air (yield-4.92 g, 89% of the theoretical yield). FDMS supported the following structure:

An absorption maximum was observed at 523 nm in the UV-visible light absorption spectrum in DMF as solvent.

Example 17

A mixture of 2,5-dianilinoterephthalic acid (3.48 g, 0.01 mol), potassium carbonate (2.76 g) and DMF (100 ml) was stirred and heated to 100° C. and 4-vinylbenzyl chloride (3.76 g, 0.11 mol) was added. Heating was continued for 1.0 hour and then the cooled reacting mixture was treated with 200 ml of water which was added dropwise. The orange product was collected by filtration, washed with water and dried in air (yield-5.58 g, 96% of the theoretical yield). FDMS supported the following expected structure:

An absorption maximum was observed at 471 nm in the UV-visible light absorption spectrum in DMF as solvent.

Example 18a

A mixture of 1,5-bis-[(1H)-1,2,4-triazolythio]anthraquinone (8.12 g, 0.02 mol), ethylene carbonate (29.4 g, 0.33 mol), ethylene glycol (30 ml) and pulverized potassium iodide (2.0 g) was heated and stirred at 125° C. for 3.5 hours. The reaction mixture was allowed to cool and water (100 ml) was added dropwise with stirring. The yellow product (1,5-bis-[[1(2-hydroxyethyl)-1,2,4-triazolyl-3-yl]thio]anthraquinone) was collected by filtration, washed with water and dried in air (yield 06.8 g, 69% of the theoretical yield).

Example 18b

A mixture of a portion (1.0 g, 0.0020 mol) of the product from Example 18a, DMF (25 ml), hydroquinone (10 mg), 4-(dimethylamino)-pyridine (49 mg) and methacrylic anhydride (0.91 ml) was stirred at room temperature and triethylamine (0.85 ml) was added dropwise. The reaction mixture was stirred at room temperature for 24 hours and then drowned into water. The yellow product was collected by filtration, washed with water and dried in air (yield-0.85 g, 67% of the theoretical yield). FDMS supported the following expected structure:

An absorption maximum at 422 nm was observed UV-visible spectrum in DMF as solvent.

Example 19a

A mixture of 1,5-bis-(cyclohexylamino)-4,8-bis-(2′-carboxyphenylthio) anthraquinone (49.5 g, 0.07 mol), ethylene carbonate (149 g, 1.69 mol), pulverized potassium iodide (42 g) and ethylene glycol (300 ml) was heated and stirred to 100° C. and held at about 110° C. for about 1.0 hour (some foaming resulted). Heating and stirring were continued at 125° C. for about 2.5 hours and the cooled reaction mixture was then drowned into 2500 ml of methanol. Some water was added to the methanol solution so further precipitate the blue solid, which was collected by filtration, washed with water and dried in air (yield-36.3 g, 62% of the theoretical yield). FDMS showed that the structure was that of the starting material for Example 19b.

Example 19b

A mixture of a portion of the 1,5-bis(cyclohexylamino)-4,8-bis-[2′-hydroxyethoxycarbonyl)-phenylthio]anthraquinone from Example 19a (1.0 g, 0.00126 mol), DMF (25 ml), hydroquinone (10 mg), DMAP (30.8 mg) and methacrylic anhydride (0.563 ml) was stirred and triethylamine (0.527 ml) was added dropwise. The reaction mixture was stirred for 24 hours at room temperature and then drowned into water (50 ml). The blue product was collected by filtration, washed with water and dried in air (yield-0.65 g, 56% of the theoretical yield). FDMS supported the following expected structure:

Absorption maxima at 603 nm and 646 nm were observed in the UV-visible absorption spectrum in DMF solution.

Example 20a Preparation of Azo Dye Coupler

A mixture of 3-acetamido-N,N-bis-(4-carboxybenzyl)aniline (12.5, 0.03 mol) (prepared as described in Example 91b of U.S. Pat. No. 6,197,223), ethylene carbonate 44 g, 0.50 mol), ethylene glycol (60 ml) and pulverized potassium iodide (2.68 g) was stirred and heated at 120–125° C. for 4.0 hours. Water (150 ml) was added drop wise with stirring to the cooled reaction mixture. The resulting solid was collected by filtration, washed with water and dried in air (yield-12.9 g, 85% of the theoretical yield). FDMS supported the following structure:

Example 20b Preparation of Intermediate Azo Dye

A mixture of 5-amino-4-cyano-3-methylisothiazole (1.39 g, 0.01 mol) and water (17.5 ml) was stirred and cooled in an ice bath. Concentrated sulfuric acid (8.3 ml) was added portionwise below about 40° C. Nitrosyl sulfuric acid (40%) (3.2 g, 0.01 mol) was then added with stirring below about 3° C. The orange solution was stirred at −2° C. to +2° C. for 2.0 hours and then added to a chilled solution of a portion (5.0 g, 0.01 mol) of the coupler from Example 20a dissolved in water (100 ml) containing concentrated sulfuric acid (10 ml) and 1:5 acid (1 part propionic acid: 5 parts acetic acid by weight) (50 ml). The coupling mixture was kept cold and the mineral acid neutralized by the addition of ammonium acetate with stirring. After being allowed to stand for about 1.0 hour with occasional stirring, the coupling mixture was drowned by the addition of water. The solid dye was collected by filtration, washed with water and dried in air. After being reslurried in hot methanol and allowing to cool, the dye was collected by filtration, washed with methanol, and dried in air (yield-3.9 g, 59% of the theoretical yield). FDMS supported the following structure:

An absorption maximum was observed at 543 nm in the UV-Visible light absorption spectrum in DMF solution.

Example 20c

A portion of the azo dye from Example 20b (0.50 g), DMF (25 ml), hydroquinone (5 mg) DMAP (19 mg) and methacrylic anhydride (0.34 ml) were mixed and stirred and triethylamine (0.32 ml) was added drop wise. After being stirred at room temperature for 24 hours, the reaction mixture was drowned into water, collected by filtration, washed with water and dried in air (yield-0.5 g). FDMS supported the following expected structure:

An absorption maximum was observed at 543 nm in the UV-visible absorption spectrum in DMF solution.

Example 21a

To p-dioxane (600 ml) was added N-(α-cyanoacetyl)piperidine (30.4 g, 0.20 mol) and the solution was stirred and cooled to about 5° C., at which temperature phosphorous oxychloride (30.6 g, 0.2 mol) was added drop-wise while keeping the temperature below 5° C. While stirring the reaction mixture at about 30° C., 1-amino-4-bromoanthraquinone (58.6 g, 0.194 mol) was added portion-wise. The reaction mixture was then heated at about 95° C. for 12 hours and then drowned into ice/water mixture. A 20% aqueous solution of sodium carbonate was added gradually until a pH of about 9 was obtained. The red product was collected by filtration washed with water are dried in air (66.3 g, 82% of the theoretical yield).

Example 21b

A portion (20.0 g, 0.050 mol) of the 6-bromo-1-cyano-2-piperidino-7H-dibenz[f,ij]-isoquinoline-7-one which was prepared in Example 21a, ethylene glycol (500 ml), dimethyl 5-aminoisophthalate (20.0 g, 0.1 mol), potassium acetate (10.0 g) and cupric acetate (10.0 g) were mixed and stirred and heated gradually to about 180° C. and held for 1.5 hours, whereupon the reaction mixture was cooled and drowned into water (800 ml). The product was collected by filtration, washed with water and dried in air (yield-46.0 g). FDMS indicated that the product consisted largely of the following structure:

Example 21c

A mixture of a portion (2.0 g, 0.0033 mol) of the product of Example 21b, DMF (25 ml), hydroquinone (20 mg), DMAP (80.6 mg) and methacrylic anhydride (1.47 ml) were mixed and stirred while triethylamine (1.4 ml) was added drop-wise. Stirring was continued at room temperature for 24 hours. The reaction mixture then was poured into methanol (50 ml) and then water (100 ml) was added to precipitate the product, which was collected by filtration, washed with water and dried in air (yield-2.2 g, 90% of the theoretical yield). FDMS indicated that the product consisted primarily of the compound having the expected structure:

The product had a magenta color when dissolved in DMF.

Example 22a

To 40% nitrosylsulfuric acid (9.6 g, 0.03 mol-100% basis) was added 1:5 acid (15 ml) with stirring at below 25° C. While cooling further, 2-chloro-4-nitroaniline (5.18 g, 0.03 mol) was added portion wise below about 8° C. Stirring was continued at about 3–8° C. for 2 hours. The diazotization reaction mixture was filtered through a fritted glass funnel to remove a few coarse particles of undissolved 2-chloro-4-nitroaniline. The diazonium salt solution was added to a chilled solution of 3-acetamido-N,N-bis-(4-carboxybenzyl) aniline (12.6 g, 0.03 mol) dissolved in 1:5 acid (120 ml) at below about 10° C. with stirring. The coupling mixture was neutralized by the portion-wise addition of ammonium acetate until neutral to Congo Red test paper and then stirred for about 1.0 hour at below 15° C. Cold water (500 ml) was added to the mixture. The solid red product was collected by filtration, washed with water and dried in air. After reslurrying in hot methanol, cooling, collecting by filtration, washing with methanol and drying in air 10.1 g (56% of the theoretical yield) of the product was obtained which had the following structure:

Example 22b

A mixture of a portion (0.60 g, 0.001 mol) of the bis-carboxy azo compound from Example 22a, potassium carbonate (0.28 g), DMF (20 ml) and 4-vinylbenzyl chloride (0.35 mol, 0.0022 mol) was stirred at about 100° C. for 2.5 hours. After cooling the reaction mixture was diluted with methanol to precipitate the product which was collected by filtration, washed with methanol and then slurried in water to remove any salts. After being collected by filtration, washed with water and dried in air, 0.35 g (42% of the theoretical yield) of product was obtained. FDMS supported mostly the following structure:

Example 23a

Thiosalicylic acid (46.3 g, 0.30 mol) was mixed with DMF (400 ml) and stirred. Potassium carbonate (82.8 g, 0.60 mol) was added and the reaction mixture was gradually heated to about 95–100° C., held for 1.5 hours. After being allowed to cool, the mixture was added portion wise to a stirred mixture of 1,5-dichloro-4,8-dinitroanthraquinone (54.9 g, 0.150 mol) and DMF (1.0 L). The reaction mixture was stirred at about 15 minutes at 10–15° C. Cooling was removed and stirring was continued at ambient temperature for 3 hours. A solution of 4-thiocresol (37.3 g, 0.3 mol) in DMF (250 ml) was added and then the whole reaction mixture was heated at about 95° C. for about 8 hours. After allowing to cool, the reaction mixture was drowned into a mixture of concentrated HCl (100 ml) water (1900 ml) and some crushed ice. The product was collected by filtration washed with water and dried in air (yield 109.8 g).

Example 23b

A mixture of 1,5-bis(2-carboxyphenylthio)-4,8-bis-(4-tolythio)-anthraquinone produced as described in Example 23a (3.78 g, 0.005 mol), ethylene carbonate (5.28 g, 0.06 mol), ethylene glycol (25 ml) and pulverized potassium iodide (1.5 g) was heated and stirred at about 125° C. for 4.0 hours. After being allowed to cool, the product was precipitated by the addition of methanol. The solid was collected by filtration, washed with methanol, and dried in air (yield-2.94 g, 70% of the theoretical yield). FDMS showed that the product consisted primarily of a compound having the structure:

Example 23c

A portion (0.5 g, 0.00059 mol) of the product from Example 23b, DMF (10 ml), DMAP (14.4 mg), hydroquinone (5 mg) and methacrylic anhydride (0.265 ml) were mixed and stirred at room temperature while triethylamine (0.248 ml) was added dropwise. Stirring was continued at room temperature for 24 hours. Methanol (50 ml) was added to the reaction mixture and then the product was precipitated by the addition of water (75 ml). The solid was collected by filtration, washed with water, and dried in air (yield-0.47 g, 81% of the theoretical yield). FDMS supported the following structure:

The product produced a bright red color when dissolved in DMF.

Example 24a

A mixture of 2,5-dianilinoterephthalic acid (20.90 g, 0.06 ml), ethylene carbonate (63.40 g, 0.72 mol), ethylene glycol (65 ml) and pulverized potassium iodide (17.5 g) was stirred and heated under nitrogen to about 120° C. Considerable foaming occurred at about 120° C. but soon subsided and the temperature was increased to about 125° C. and stirring continued for 3.5 hours. The reaction mixture was cooled and methanol (100 ml) was added to the reaction mixture dropwise. The orange solid which crystallized was collected by filtration, washed with water and dried in water (yield-14.4 g, 55% of the theoretical yield). FDMS showed that the product was the bis-(2-hydroxyethyl) ester having the formula:

Example 24b

The orange diol colorant as prepared in Example 24a (50.0 g, 0.115 mol), acetone (150 ml), DMAP (2 g), t-butylhydroquinone (1 g) and triethylamine (50 g) were mixed together and the mixture was stirred and heated to 40° C. and methacrylic anhydride (50 g) was added dropwise. A slight exotherm was observed and heating was continued for 1.0 hours. The reaction solution was allowed to cool and water (150 ml) was added drop wise over about 30 minutes to precipitate the product which was collected by filtration, washed with water and dried at about 60–70° C. under vacuum. The yield of bright orange solid was 45.0 g, 66% of the theoretical yield. FDMS supported the following structure:

Additional examples of the colorant compounds which contain one or more ethylenically-unsaturated (vinyl), photopolymerizable radicals according to the present invention are set forth in the examples of Tables I–XIV. These compounds may be prepared by procedures analogous to those described in the preceding examples and/or by published techniques.

TABLE I Azo Colorants of Formula XIII

Example No. D R₁₅ R₁₆ R₁₇ 25 4-NO₂-phenyl H —CH₂—C₆H₄-4-CO₂—CH₂CH₂— —CH₂—C₆H₄-4-CO₂—CH₂CH₂— OCOC(CH₃)═CH₂ OCOC(CH₃)═CH₂ 26 2-Cl-4-NO₂-phenyl 3-CH₃ —CH₂—C₆H₄-4-CO₂—CH₂CH₂— —CH₂—C₆H₄-4-CO₂—CH₂CH₂— OCOC(CH₃)═CH₂ OCOC(CH₃)═CH₂ 27 2-Br-4-CN-phenyl 3-NHCOCH₃ —CH₂—C₆H₄-4-CO₂—CH₂CH₂— —CH₂—C₆H₄-4-CO₂—CH₂CH₂— OCOC(CH₃)═CH₂ OCOC(CH₃)═CH₂ 28 2,6-di-CN-4-NO₂-phenyl 3-NHCOCH₃ —CH₂—C₆H₄-4-CO₂—CH₂CH₂— —CH₂—C₆H₄-4-CO₂—CH₂CH₂— OCOC(CH₃)═CH₂ OCOC(CH₃)═CH₂ 29 2-Br-4,6-di-NO₂-phenyl 2-OCH₃-5-NHCOCH₃ —CH₂—C₆H₄-4-CO₂—CH₂CH₂— —CH₂—C₆H₄-4-CO₂—CH₂CH₂— OCOC(CH₃)═CH₂ OCOC(CH₃)═CH₂ 30 2-Cl-4-CH₃SO₂-phenyl 3-NHCOCH₃ —C₂H₅ —CH₂—C₆H₄-4-CO₂—CH₂CH₂— OCOC(CH₃)═CH₂ 31 2-CN-4-CH₃SO₂-phenyl 3-NHCOCH₃ —C₂H₅ —CH₂—C₆H₄-4-CO₂—CH₂CH₂— OCOC(CH3)═CH₂ 32 2-CN-4-CH₃SO₂-phenyl 3-CH₃ —C₂H₅ —CH₂CH₂O—C₆H₃-3,5-bis- (—CO₂CH₂—C₆H₄-4-CH═CH₂) 33 2-Br-4-NO₂-phenyl 3-NHCOCH₃ —CH₂—C₆H₄-4-(CO₂—CH₂— —CH₂—C₆H₄-4-(CO₂—CH₂— C₆H₄-4-CH═CH₂) C₆H₄-4-CH═CH₂) 34 5-C₂H₅S-1,3,4- 3-NHCOCH₃ —CH₂—C₆H₄-4-(CO₂—CH₂— —CH₂—C₆H₄-4-(CO₂—CH₂— thiadiazol-2-yl C₆H₄-4-CH═CH₂) C₆H₄-4-CH═CH₂) 35 6-CH₃SO₂- 3-NHCOCH₃ —CH₂—C₆H₄-4-(CO₂—CH₂— —CH₂—C₆H₄-4-(CO₂—CH₂— benzothiazol-2-yl C₆H₄-4-CH═CH₂) C₆H₄-4-CH═CH₂) 36 5,6-di-Cl- 3-NHCOCH₃ —CH₂—C₆H₄-4-(CO₂—CH₂— —CH₂—C₆H₄-4-(CO₂—CH₂— benzothiazol-2-yl C₆H₄-4-CH═CH₂) C₆H₄-4-CH═CH₂) 37 5-NO₂-benzothiazol-2-yl 3-NHCOCH₃ —CH₂—C₆H₄-4-(CO₂—CH₂— —CH₂—C₆H₄-4-(CO₂—CH₂— C₆H₄-4-CH═CH₂) C₆H₄-4-CH═CH₂) 38 4-Br-3-CH₃-iso- 3-NHCOCH₃ —CH₂—C₆H₄-4-(CO₂—CH₂— —CH₂—C₆H₄-4-(CO₂—CH₂— thiazol-5-yl C₆H₄-4-CH═CH₂) C₆H₄-4-CH═CH₂) 39 3-CH₃-4-CN-iso- 3-NHCOCH₃ —CH₂—C₆H₄-4-(CO₂—CH₂— —CH₂—C₆H₄-4-(CO₂—CH₂— thiazol-5-yl C₆H₄-4-CH═CH₂) C₆H₄-4-CH═CH₂) 40 3-SCH₃-1,2,4- H —CH₂CH₂—CO₂—CH₂CH₂— —CH₂CH₂—CO₂—CH₂CH₂— thiadiazol-5-yl OCO(CH3)═CH2 OCO(CH3)═CH2 41 5-NO₂-thiazol-2-yl 3-CH₃ —CH₂CH₂O—C₆H₄-2-(CO₂— —C₂H₅ CH₂—C₆H₄-4-CH═CH₂) 42 2-CH₃CO-4-NO₂₋ 3-NHCOCH₃ —CH₂CH₂S—C₆H₄-2-(CO₂— —C₂H₅ thien-5-yl CH₂CH₂—C₆H₄-4-CH═CH₂) 43 4-CH₃CO-2-NO₂- 3-CH₃ —CH₂CH₂S—C₆H₄-2-(CO₂— —CH₂CH₂S—C₆H₄-2-(CO₂— thien-5-yl CH₂—C₆H₄-4-CH═CH₂) CH₂—C₆H₄-4-CH═CH₂) 44 2,4-di-CH₃O₂C-4- H —CH₂CH₂O—C₆H₄-2-(CO₂— —C₂H₅ CH₃-thien-5-yl CH₂CH₂OCO—CH═CH₂) 45 5-NO₂-benziso- 3-NHCOC₂H₅ —CH₂—C₆H₄-4-(CO₂— —C₂H₅ thiazol-3-yl CH₂CH₂CH₂OCO═CH₂) 46 4-phthalimidyl 3-NHCOCH₃ —CH₂CH₂SO₂—C₆H₄-2-(CO₂— CH₂—CH(CH₃)—OCO—CH═CH₂) 47 4-Br-N-C₂H₅-5-phthalimidyl 3-CH₃

—C₂H₅

TABLE II Methine Colorants of Formula XV

Example No. AM R₁₅ R₁₆ R₁₇ 48 ═C(CN)CN H —C₂H₅ —CH₂—C₆H₄-4-(CO₂—CH₂CH₂— OCOC(CH3)CH═CH₂) 49 ═C(CN)SO₂CH₃ 3-CH₃ —CH₂—C₆H₄-4-(CO₂—CH₂CH₂— —CH₂—C₆H₄-4-(CO₂—CH₂CH₂— OCOC(CH3)CH═CH₂) OCOC(CH3)CH═CH₂) 50 ═C(CN)CO₂CH₃ 3-CH₃ —CH₂CH₂O—C₆H₃-3,5-bis- —C₂H₅ (—CO₂CH₂—C₆H₄-4-CH═CH₂) 51 ═C(CN)CONH₂ 3-CH₃ —C₂H₅ —CH₂CH₂S—C₆H₄-2-(CO₂— CH₂C₆H₄-4-CH═CH₂) 52 ═C(CN)CO₂C₂H₅ 3-CH₃ —CH₂C₆H₅ —CH₂—C₆H₄-4-(CO₂—CH₂— C₆H₄-4-CH═CH₂) 53 ═C(CN)CN 3-CH₃

—C₂H₅ 54 ═C(CN)CO₂CH₃ 3-CH₃ —CH₂CH₂S—C₆H₄-2-(CO₂— —CH₃ CH₂—C₆H₄-4-CH═CH₂) 55 ═C(CN)CN 2,5-di-OCH₃ —CH₂—C₆H₄-4-(CO₂—CH₂CH₂— —CH₂CH₂O—C₆H₄-2-(CO₂— OCOC(CH3)CH═CH₂) CH₂CH₂—OCO—CH═CH₂) 56 ═C(CN)CO₂C₂H₅ H —CH₂CH₂—CO₂CH₂—C₆H₄— —CH₂CH₂—CO₂CH₂—C₆H₄— 4-CH═CH₂ 4-CH═CH₂

TABLE III 3-Aryl-2,5-Dioxypyrroline Colorants of Formula XVII

Example No. R₁₅ R₁₆′ R₁₇ 57 H —CH₂CH₃ H —CH₂—C₆H₄-4-(CO₂—CH₂CH₂— OCOC(CH3)═(CH₂) 58 H —CH₂CH₃ —CH₃ —C₆H₄-4-(CO₂—CH₂—C₆H₄-4-CH═CH₂) 59 H —CH₂—C₆H₄-4-(CO₂—CH₂—C₆H₄— —C₂H₅ —CH₂—C₆H₄-4-(CO₂—CH₂—C₆H₄— 4-CH═CH₂) 4-CH═CH₂) 60 H —CH₂CH₂S—C₆H₄-2-(CO₂—CH₂CH₂— —CH₂C₆H₅ —CH₂CH₂S—C₆H₄-2-(CO₂—CH₂CH₂— OCOC(CH3)═CH₂) OCOC(CH3)═CH₂) 61 H —CH₂CH₂O—C₆H₃-3,5-bis-(—CO₂CH₂— H —C₂H₅ C₆H₄-4-CH═CH₂) 62 —CH₃ —CH₂—C₆H₄-4-(CO₂—CH₂CH₂— R₁₆ —C₂H₅ OCOCH═CH₂)

TABLE IV ANTHRAQUINONE COLORANTS OF FORMULA XXa

Example No. R₂₈ L₄ X 63 H 1-NH— —CH₂—C₆H₄-4-CH═CH₂ 64 H 2,7-di-S— —CH₂—C₆H₄-4-CH═CH₂ 65 H 1,5-di-NH— —CH₂—C₆H₄-4-CH═CH₂ 66 H 1,8-di-NH— —CH₂—C₆H₄-4-CH═CH₂ 67 H 1,5-di-S— —CH₂—C₆H₄-4-CH═CH₂ 68 H 1,5-di-S— —CH₂CH(CH₃)OCOC(CH₃)═CH₂ 69 H 1,5-di-NH— —CH₂—CH(OH)CH₂—OCONH— CH₂CH₂OCOCH═CH₂ 70 1-NH₂-2-Br 4-NH —CH₂—C₆H₄-4-C(CH₃)═CH₂ 71 1-NH₂-2-SO₂C₆H₅ 4-NH —CH₂CH(CH₃)OCOCH═CH₂ 72 1-NH₂-2-S—C₆H₅ 4-NH —CH₂CH₂CH₂OCOC(CH₃)═CH₂ 73 1-NH₂-2-CN 4-NH —(CH₂)₄—OCONHCOC(CH₃)═CH₂ 74 1-NHCH₃ 4-NH —CH₂C(CH₃)₂CH₂OCOC(CH₃)═CH₂ 75 1-NHCH₂CH(CH₃)₂ 4-S— —CH₂—C₆H₁₀-4-(CH₂OCOC(CH₃)═CH₂) 76 1-NH₂-4-OH 2-O— —(CH₂)₄—OCOCH═CH₂ 77 H 1,4-di-S— —CH₂-1,4-C₆H₄CH═CH₂ 78 1-NH₂-4-NHC₆H₅ 2-S— —CH₂CH₂OCONHC(CH₃)₂—C₆H₄- 3-C(CH₃)═CH₂ 79 1-NH2, 4-S-benzo- 2-SO₂— —CH₂—1,4-C₆H₄—CH═CH₂ thiazol-2-yl 80 1,5-di-S—C₆H₅ 4,8-di-S— —CH₂CH(CH₃)—OCOC(CH₃)═CH₂ 81 1,8-di-NH₂-4,5- 2,7-di-O— —CH₂CH₂OCH₂CH₂OCOC(CH₃)═CH₂ di-OH 82 1,8-di-NH₂-4,5-di-OH 2,5-di-S—

83 1,8-di-OH 4,5-di-S— —CH₂CH₂(OCH₂CH₂)₃OCOC(CH₃)═CH₂

TABLE V Anthraquinone Colorants of Formula XXb

Example No. R₂₈ R₂₉ L₄ —CO₂X 84 H H 1-S— 2′-CO₂CH₂CH(CH₃)OCOC(CH₃)═CH₂ 85 H H 1,5-di-NH— 2′-CO₂CH₂CH(CH₃)OCOCH═CH₂ 86 H 4′-Br 1,5-di-NH— 2′-CO₂CH₂CH(CH₃)OCONHC(CH₃)₂—C₆H₄- 3-C(CH₃)═CH₂ 87 H H 1,5-di-S— 3′-CO₂CH₂CH₂OCOC(CH₃)═CH₂ 88 H H 1,8-di-S— 4′-CO₂CH₂CH₂CH₂OCOCH═CH—CO₂H 89 H 2′-CH₃ 1,4-di-S— 4′—CO₂CH₂—C₆H₄-4-CH═CH₂ 90 H H 1,4,5,8-tetra-S— 2′-CO₂CH₂CH(CH₃)OCOC(CH₃)═CH₂ 91 1,5-di-NH— H 4,8-di-S— 2′-CO₂CH₂CH(CH₃)OCOC(CH₃)═CH₂ C₆H₁₁ 92 1-NH₂-2-Br H 4-NH— 2′-CO₂CH₂CH(CH₃)OCOC(CH₃)═CH₂ 93 1-NH₂-2-OCH₃ H 4-S— 2′-CO₂CH₂—C₆H₄-4-C(CH₃)═CH₂ 94 1-NH₂-2- H 4-NH— 2′-CO₂CH₂CH(CH₃)OCOC(CH₃)═CH₂ SO₂C₆H₅ 95 1-NH₂-4- H 2-O— 4′CO₂CH₂CH(OH)CH₂OCOCH═CH₂ NHSO₂CH₃ 96 1-NH₂-2-CF₃ H 4-S— 3′-CO₂CH₂—C₆H₄-4-CH═CH₂ 97 1,4-di-OH H 2-S— 2′-CO₂(CH₂)₆OCOC(CH₃)═CH₂ 98 1,8-di-NH₂-4,5- H 2,7-di-S— 2′-CO₂CH₂CH(CH₃)OCOC(CH₃)═CH₂ di-OH 99 5,8-di-S-C₆H₅ H 1,4-di-S— 2′CO₂CH₂CH(CH₃)OC-1,3-C₆H₄—CH═CH₂ 100 1,4-bis-(2,6- H 6,7-di-S— 2′-CO₂CH₂CH(CH₃)OCOC(CH₃)═CH₂ diethylanilino)

TABLE VI ANTHRAQUINONE COLORANTS OF FORMULA XXe

Example No. R₂₈ Position R Y 101 H 1- H —CH₂—C₆H₄-4-CH═CH₂ 102 H 1,8-di H —CH₂CH₂OCOC(CH₃)═CH₂ 103 H 1,4,5,8-tetra H —CH₂CH₂OCOCH═CH₂ 104 4,5-bis-(—SC₆H₄-4-CH₃) 1,8-di —CH₃ —CH₂CH₂OCOC(CH₃)═CH₂ 105 H 1,5-di —C₆H₅ —CH₂CH(CH₃)OCOCH═CH₂ 106 1-NH₂-2-Br 4- H —CH₂—C₆H₄-4-CH═CH₂ 107 1-NH₂ 2,4-di H —CH₂CH₂OCOC(CH₃)═CH₂ 108 1-NH₂-4-OH 2- H —CH₂CH₂OCONHC(CH₃)₂— C₆H₄-3-C(CH₃)═CH₂ 109 1,8-di-NH₂-4,5-di-OH 2,7-di H —CH₂CH₂OCOC(CH₃)═CH₂ 110 1,4-bis-(2,6-diethyl- 6,7-di H —(CH₂)₆—OCOC(CH₃)═CH₂ anilino) 111 1,4-bis-(2,4,6-tri- 6,7-di H —CONHCOC(CH₃)═CH₂ methylanilino) Position = Position of triazolythio radical(s):

on anthraquinone nucleaus of Formula XXe.

TABLE VII Anthrapyridone Colorants of Formula XXIa

Example No. R₂₈ R₃₀ R₃₁ L₄ X 112 H —CH₃ H -6-NH— —CH₂—C₆H₄-4-CH═CH₂ 113 H —CH₃ H -6-NH— —CH₂CH₂OCOC(CH₃)═CH₂ 114 H —CH₃ H -6-NH— —CH₂CH₂OCOCNHC(CH₃)₂—C₆H₄- 4-C(CH₃)═CH₂ 115 H —CH₃ —CN -6-NH— —CH₂CH(CH₃)OCOC(CH₃)═CH₂ 116 H —CH₃ —CN -6-NH— —CH₂CH(OH)CH₂OCOCH═CH₂ 117 H —C₄H₉-n —CO₂C₂H₅ -6-NH— —CH₂—C₆H₄-4-CH═CH₂ 118 H —CH₃ —CO₂C₂H₅ -6-NH— —CH₂CH₂OCONHCOC(CH₃)═CH₂ 119 4-Br H —CO₂C₂H₅ -6-NH— —CH₂CH₂CH₂OCOC(CH₃)═CH₂ 120 4-SO₂C₆H₅ H —CO₂C₂H₅ -6-NH— —CH₂—C₆H₄-4-CH═CH₂ 121 4-S—C₆H₅ H —CO₂C₂H₅ -6-NH—

122 4-CH₃ H —COCH₃ -6-NH— —CH₂CH₂OCH₂CH₂OCOCH═CH₂ 123 4-OC₆H₅ H —COC₆H₅ -6-NH— —CH₂—C₆H₄-4-CH═CH₂ 124 H —CH₃ —CO₂C₂H₅ 4,6-di-S— —CH₂—C₆H₄-4-CH═CH₂ 125 6-NHC₆H₅ —CH₃ —CO₂C₂H₅ 4-O— —CH₂—C₆H₄-4-CH═CH₂ 126 6-NHC₆H₅ —CH₃ —CO₂C₂H₅ 4-S— —CH₂CH₂OCOC(CH₃)═CH₂ 127 H —C₆H₅ —CN 6-S— —CH₂CH₂OCNH(CH₂)₆— OCO(CH3)═CH₂

TABLE VIII Anthrapyridone Colorants of Formula XXIb

Example No. R₂₈ R₂₉ R₃₀ R₃₁ L₄ —CO₂X 128 H H —CH₃ H 6-NH— 2′-CO₂CH₂—C₆H₄-4-CH═CH₂ 129 H H —CH₃ H 6-S— 2′-CO₂CH₂—C₆H₄-4-CH═CH₂ 130 H 4′-Br —CH₃ H 6-NH— 2′-CO₂CH₂CH₂OCOC(CH₃)═CH₂ 131 H 2′-CH₃ —CH₃ H 6-NH— 4′-CO₂CH₂CH(CH₃)— OCOC(CH₃)═CH₂ 132 H H —CH₃ —CO₂C₂H₅ 4-S-,6-NH— 2′-CO₂CH₂CH₂OCH₂CH₂— OCOCH═CH₂ 133 H H —CH₃ —CO₂C₂H₅ 6-S— 4′-CO₂CH₂—C₆H₄-4-CH═CH₂ 134 4-Br H H —CO₂C₂H₅ 6-NH— 3′-CO₂CH₂CH₂OCOC(CH₃)═CH₂ 135 4-SO₂—CH₃ H H —CO₂C₂H₅ 6-NH— 2′-CO₂CH₂—C₆H₁₀-4- (CH₂OCOCH═CH₂) 136 4-S—C₆H₁₁ H H —CO₂C₂H₅ 6-NH— 2′-CO₂CH₂C(CH₃)₂CH₂— OCOC(CH₃)═CH₂ 137 H H H 2-benzoxazolyl 6-NH— 2′-CO₂CH₂CH₂OCOC(CH₃)═CH₂ 138 H H H 2-benzothiazolyl 6-NH— 2′-CO₂CH₂CH₂OCOC(CH₃)═CH₂ 139 H H —C₆H₁₁ —SC₆H₅ 6-NH— 2′-CO₂CH₂CH₂OCOC(CH₃)═CH₂ 140 H H —CH₂C₆H₅ —SO₂C₆H5 6-NH— 2′-CO₂CH₂CH₂OCOC(CH₃)═CH₂ 141 H H —CH₂CH₂—OCH₃ —Cl 6-NH— 2′-CO₂CH₂CH₂OCOC(CH₃)═CH₂

TABLE IX Anthrapyridine Colorants of Formula XXIIa

Example No. R₂₈ R₃₁ R₃₂ L₄ X 142 H —CN —N(CH₃)₂ 6-NH— —CH₂1,4-C₆H₄—CH═CH₂ 143 H —CN —N(C₂H₅)₂ 6-NH— —CH₂CH₂OCOC(CH₃)═CH₂ 144 H —CN —N(CH₃)C₆H₅ 6-NH— —CH₂CH(CH₃)OCOCH═CH₂ 145 H —CN Piperidino 6-NH— —CH₂CH₂OCNHC(CH₃)₂—C₆H₄- 3-C(CH₃)═CH₂ 146 H —CN Morpholino 6-NH— —CH₂C(CH₃)₂CH₂OCOC (CH₃)═CH₂ 147 H —CN Pyrrolidino 4-S-,6-NH —CH₂CH₂OCO—C₆H₄-4-CH═CH₂ 148 H —CN —N(CH₂CH₂OCH₃)₂ 4-S-,6-NH —CH₂CH₂OCOC(CH₃)₂— NHCOC(CH₃)═CH₂ 149 H —CN —N(CH₃)C₆H₁₁ 6-S— —CH₂CH₂OCOCH═CH—CO₂H 150 H —CN —N(CH₃)C₂H₅ 4,6-di-S— —(CH₂)₆OCOCH═CH—CO₂C₂H₅ 151 4-Br —CN —N(C₂H₅)C₆H₅ 6-NH —CH₂—C₆H₁₀-4-(CH₂OCO CH═CH₂) 152 4-SO₂—C₆H₅ —CN —N(CH₃)₂ 4-NH —CH₂CH(OH)CH₂OCOCH═CH₂ 153 4-CF₃ —CN —N(CH₃)₂ 6-NH —CH₂CH₂(OCH₂CH₂)₃OCOCH═CH₂ 154 H H H 6-NH —CH₂CH(CH₃)OCOC(CH₃)═CH₂ 155 H C₆H₅ CH₃ 6-NH —CH₂CH(CH₃)CH₂OCOCH═CH₂

TABLE X Anthrapyridine Colorants of Formula XXIIb

Example No. R₂₈ R₂₉ R₃₁ R₃₂ L₄ —CO₂X 156 H H —CN Piperidino -6-NH 2′-CO₂CH₂-1,4-C₆H₄—CH═CH₂ 157 H 4′-Br —CN Morpholino -6-NH 2′-CO₂CH₂CH₂OCOC(CH₃)═CH₂ 158 H 4′-CH₃ —CN Pyrrolidino -6-NH 3′-CO₂CH₂CH(CH₃)OCOCH═CH₂ 159 H H —CN —N(CH₃)₂ -6-NH 4′-CO₂(CH₂)₃OCOC(CH₃)═CH₂ 160 H H —CN —N(CH₃)C₆H₅ -4-S-6-NH— 2′-CO₂CH₂CH₂OCOC(CH₃)═CH₂ 161 4-Br H —CN —N(CH₃)C₂H₅ 6-S— 2′-CO₂CH₂-1,4-C₆H₄—CH═CH₂ 162 4-SO₂CH₃ H —CN —N(CH₃)C₆H₁₁ 4-SO₂-6-NH— 2′CO₂CH₂C(CH₃)₂CH₂— OCOC(CH₃)═CH₂ 163 4-CN H —CN —N(CH₂CH₂—OC₂H₅)₂ 6-NH— 3′-CO₂CH₂CH₂OCOCH═CH—CO₂H 164 4-OCH₃ H —CN —N(C₂H₅)C₆H₅ 6-NH— 4′-CO₂CH₂—C₆H₄-4-CH═CH₂ 165 6-NHC₆H₅ H —CN —N(C₂H₅)₂ 4-S— 2′CO₂CH₂—C₆H₄-4-C(CH₃)═CH₂ 166 4-SO₂—N(CH₃)₂ H —CN —N(C₂H₅)₂ 4-S— 2′CO₂CH₂—C₆H₄-4-C(CH₃)═CH₂ 167 4-CH₃ H —CN —N(C₂H₅)₂ 4-S— 2′CO₂CH₂—C₆H₁₀-4- (OCOC(CH₃)═CH₂) 168 H H —CO₂CH₃ —N(C₂H₅)₂ 6-NH— 2′CO₂CH₂CH₂OCH₂CH₂— OCOCH═CH₂ 169 H H H —C₆H₅ 6-NH— 2′CO₂CH₂CH(OH)CH₂— OCOCH═CH₂ 170 H H —CH₃ H 6-NH— 2′CO₂CH₂CH(OH)CH₂— OCOCH═CH₂ 171 H H —C₆H₅ —CH₃ 6-NH— 2′CO₂CH₂CH(OH)CH₂— OCOCH═CH₂

TABLE XI Quinophthalone Colorants of Formula XXIII

Example No. R₃₅ X 172 H —CH₂CH₂OCOC(CH₃)═CH₂ 173 H —CH₂CH₂OCONHC(CH₃)₂—C₆H₄-3-C(CH₃)═CH₂ 174 H —CH₂CH(CH₃)OCOCH═CH₂ 175 H —CH₂CH(OH)CH₂OCOC(CH₃)═CH₂ 176 Br —CH₂CH₂OCOC(CH₃)═CH₂ 177 Br —CH₂CH₂OCONHC(CH₃)₂—C₆H₄-3-C(CH₃)═CH₂ 178 Br —CH₂—C₆H₄-4-CH═CH₂ 179 —SO₂C₆H₅ —CH₂CH₂OCOC(CH₃)═CH₂ 180 —SO₂—C₆H₄-4-CH₃ —CH₂CH₂OCONHCOC(CH₃)═CH₂ 181 —S—C₆H₄—CH₃ —CH₂C(CH₃)₂CH₂OCOC(CH₃)═CH₂ 182 2-benzothiazolyl —CH₂—C₆H₁₀-4-(CH₂OCOC(CH₃)═CH₂) 183 2-benzoxazolyl —CH₂CH₂O—C₆H₄-4- (OCH₂CH₂OCOC(CH₃)═CH₂) 184 1,2,4-triazol-3-ylthio —CH₂—C₆H₄-4-(CH₂OCOCH═CH₂) 185 —S—C₆H₄-2-(CO₂CH₂CH₂OCOCH═CH₂) —CH₂CH₂OCOCH═CH₂

TABLE XII Nitroarylamine Colorants of Formula XXIV

Example No. R₃₆ R₃₇ R₃₈

CO₂X)₀₋₂ 186 H —CH₃ —CH₃ 4-CO₂CH₂CH₂OCOC(CH₃)═CH₂ 187 H —CH₂CH₂ —CH₂CH₃ 3-CO₂CH₂CH(CH₃)OCOCH═CH₂ 188 H —CH₂CH₃ —CH₃ 3,5-di-CO₂CH₂CH₂— OCOC(CH₃)═CH₂ 189 H —C₆H₅ —CH₃ 2,5-di-CO₂(CH₂)₆OCOC(CH₃)═CH₂ 190 H —C₄H₉—n H 2-CO₂CH₂—C₆H₄-4-CH═CH₂ 191 H —C₆H₁₁ H 2-CO₂CH₂CH₂OCONHC(CH₃)₂— C₆H₄-3-C(CH₃)═CH₂ 192 H —C₆H₅ H 2-CO₂CH₂CH₂OCOCH═CH—CO₂H 193 H —C₆H₄-2-(CO₂CH₂CH₂— H H OCOCH═CH₂) 194 H —C₆H₃-3,5-bis(CO₂CH₂— H H C₆H₄—CH═CH₂) 195 H —C₆H₄-2-(CO₂CH₂CH₂— H 2-(CO₂CH₂CH₂OCOC(CH₃)═CH₂) OCOC(CH₃)═CH₂)

TABLE XIII Diarylamino Terephthlate Colorants of Formula XXIX

Example No. R₄₀ X 196 H —CH₂C(CH₃)₂CH₂OCOC(CH₃)═CH₂ 197 H —CH₂—C₆H₁₀-4-(CH₂—OCOCH═CH₂) 198 H —CH₂CH₂(OCH₂CH₂)₂OCOC(CH₃)═CH₂ 199 H —CH₂CH(CH₃)OCOC(CH₃)═CH₂ 200 H —CH₂CH(OH)CH₂OCOCH═CH₂ 201 H —CH₂CH₂OCONHC(CH₃)₂—C₆H₄-3-C(CH₃)═CH₂ 202 H —CH₂CH₂OCONHCOC(CH₃)═CH₂ 203 4-CH₃ —CH₂CH₂OCOC(CH₃)═CH₂ 204 4-Cl —CH₂—C₆H₄-4-CH═CH₂ 205 4-Br —CH₂CH(CH₃)OCOCH═CH₂ 206 3-C₂H₅ —CH₂CH₂OCONH(CH₂)₆OCOC(CH₃)═CH₂ 207 4-C₆H₅ —CH₂CH₂OCOCH═CH—C₆H₅ 208 2-CH₃ —CH₂CH₂OCOCH═CH—CH₃ 209 2,5-di-CH₃ —CH₂CH₂OCOCH═CH—CO₂H 210 4-OC₂H₅ —CH₂CH₂OCOC(CH₃)₂NHCOC(CH₃)═CH₂

TABLE XIV Miscellaneous Colorants EXAMPLE 211

EXAMPLE 212

EXAMPLE 213

EXAMPLE 213

EXAMPLE 214

EXAMPLE 215 2(3), 16(17)-di-[CO₂CH₂CH₂—OCOC(CH₃)═CH_(2])—PcCu Pc = phthalocyanine EXAMPLE 216 2(3), 9(10), 16(17), 23(24)-Tetra[2′-CO₂CH₂CH₂—O—COC(CH₃)═CH₂)phenoxy]—PcCu Pc = Phthalocyanine

The functionalized dyes or colorants which contain vinyl or substituted vinyl groups are polymerizable or copolymerizable, preferably by free radical mechanisms, said free radicals being generated by exposure to UV light by methods known in the art of preparing UV-cured resins. Polymerization can be facilitated by the addition of photoinitiators. The colored polymeric materials normally are prepared by dissolving the functionalized colorants containing copolymerizable groups in a polymerizable vinyl monomer with or without another solvent and then combining with an oligomeric or polymeric material which contains one or more vinyl or substituted vinyl groups.

The eighth embodiment of the present invention is a coating composition comprising (i) one or more polymerizable vinyl compounds, i.e., vinyl compounds which are copolymerizable with the dye compounds described herein, (ii) one or more of the dye compounds described above, and (iii) at least one photoinitiator. The polymerizable vinyl compounds useful in the present invention contain at least one unsaturated group capable of undergoing polymerization upon exposure to UV radiation in the presence of a photoinitiator, i.e., the coating compositions are radiation-curable. Examples of such polymerizable vinyl compounds include acrylic acid, methacrylic acid and their anhydrides; crotonic acid; itaconic acid and its anhydride; cyanoacrylic acid and its esters; esters of acrylic and methacrylic acids such as allyl, methyl, ethyl, n-propyl, isopropyl, butyl, tetrahydrofurfuryl, cyclohexyl, isobornyl, n-hexyl, n-octyl, isooctyl, 2-ethylhexyl, lauryl, stearyl, and benzyl acrylate and methacrylate; and diacrylate and dimethacrylate esters of ethylene and propylene glycols, 1,3-butylene glycol, 1,4-butanediol, diethylene and dipropylene glycols, triethylene and tripropylene glycols, 1,6-hexanediol, neopentyl glycol, polyethylene glycol, and polypropylene glycol, ethoxylated bisphenol A, ethoxylated and propoxylated neopentyl glycol; triacrylate and trimethacrylate esters of tris-(2-hydroxyethyl)isocyanurate, trimethylolpropane, ethoxylated and propoxylated trimethylolpropane, pentaerythritol, glycerol, ethoxylated and propoxylated glycerol; tetraacrylate and tetramethacrylate esters of pentaerythritol and ethoxylated and propoxylated pentaerythritol; acrylonitrile; vinyl acetate; vinyl toluene; styrene; N-vinyl pyrrolidinone; alpha-methylstyrene; maleate/fumarate esters; maleic/fumaric acid; crotonate esters, and crotonic acid.

The polymerizable vinyl compounds useful in the present invention include polymers which contain unsaturated groups capable of undergoing polymerization upon exposure to UV radiation in the presence of a photoinitiator. The preparation and application of these polymerizable vinyl compounds are well known to those skilled in the art as described, for example, in Chemistry and Technology of UV and EB Formulation for Coatings, Inks, and Paints, Volume II: Prepolymers and Reactive Diluents, G. Webster, editor, John Wiley and Sons, London, 1997. Examples of such polymeric, polymerizable vinyl compounds include acrylated and methacrylated polyesters, acrylated and methacrylated polyethers, acrylated and methacrylated epoxy polymers, acrylated or methacrylated urethanes, acrylated or methacrylated polyacrylates (polymethacrylates), and unsaturated polyesters. The acrylated or methacrylated polymers and oligomers typically are combined with monomers which contain one or more acrylate or methacrylate groups, e.g., monomeric acrylate and methacrylate esters, and serve as reactive diluents. The unsaturated polyesters, which are prepared by standard polycondensation techniques known in the art, are most often combined with either styrene or other monomers, which contain one or more acrylate or methacrylate groups and serve as reactive diluents. A second embodiment for the utilization of unsaturated polyesters that is known to the art involves the combination of the unsaturated polyester with monomers that contain two or more vinyl ether groups or two or more vinyl ester groups (WO 96/01283, WO 97/48744, and EP 0 322 808).

The coating compositions of the present invention optionally may contain one or more added organic solvents if desired to facilitate application and coating of the compositions onto the surface of substrates. Typical examples of suitable solvents include, but are not limited to ketones, alcohols, esters, chlorinated hydrocarbons, glycol ethers, glycol esters, and mixtures thereof. Specific examples include, but are not limited to acetone, 2-butanone, 2-pentanone, ethyl acetate, propyl acetate, isopropyl acetate, butyl acetate, isobutyl acetate, ethylene glycol diacetate, ethyl 3-ethoxypropionate, methyl alcohol, ethyl alcohol, propyl alcohol, isopropyl alcohol, butyl alcohol, ethylene glycol, propylene glycol, ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol monopropyl ether, ethylene glycol monobutyl glycol, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, diethylene glycol monobutyl ether, propylene glycol monomethyl ether, diethylene glycol monobutyl ether acetate, diethylene glycol monoethyl ether acetate, ethylene glycol monobutyl ether acetate, propylene glycol monomethyl ether acetate, methylene chloride, chloroform, and mixtures thereof. The amount of added or extraneous solvent which may be present in our novel coating compositions may be in the range of about 1 to 70 weight percent, more typically about 1 to 25 weight percent, based on the total weight of the coating composition.

Certain polymerizable vinyl monomers may serve as both reactant and solvent. These contain at least one unsaturated group capable of undergoing polymerization upon exposure to UV radiation in the presence of a photoinitiator. Specific examples include, but are not limited to: methacrylic acid, acrylic acid, ethyl acrylate and methacrylate, methyl acrylate and methacrylate, hydroxyethyl acrylate and methacrylate, diethylene glycol diacrylate, trimethylolpropane triacrylate, 1,6 hexanediol di(meth)acrylate, neopentyl glycol diacrylate and methacrylate, vinyl ethers, divinyl ethers such as diethyleneglycol divinyl ether, 1,6-hexanediol divinyl ether, cyclohexanedimethanol divinyl ether, 1,4-butanediol divinyl ether, triethyleneglycol divinyl ether, trimethylolpropane divinyl ether, and neopentyl glycol divinyl ether, vinyl esters, divinyl esters such as divinyl adipate, divinyl succinate, divinyl glutarate, divinyl 1,4-cyclohexanedicarboxylate, divinyl 1,3-cyclohexanedicarboxylate, divinyl isophthalate, and divinyl terephthalate, N-vinyl pyrrolidone, and mixtures thereof.

In addition, the compositions of the present invention may be dispersed in water rather than dissolved in a solvent to facilitate application and coating of the substrate surface. In the water-dispersed compositions of the present invention a co-solvent is optionally used. Typical examples of suitable cosolvents include but are not limited to acetone, 2-butanone, methanol, ethanol, isopropyl alcohol, ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol monopropyl ether, and ethylene glycol monobutyl ether, ethylene glycol, and propylene glycol. Typical examples of water-soluble ethylenically unsaturated solvents include but are not limited to: methacrylic acid, acrylic acid, N-vinyl pyrrolidone, 2-ethoxyethyl acrylate and methacrylate, polyethylene glycol dimethacrylate, polypropylene glycol monoacrylate and monomethacrylate, and mixtures thereof. The amount of suitable aqueous organic solvent (i.e., organic solvent and water) in the dispersed coating compositions of the present invention is about 10 to about 90 weight percent, preferably about 75 to about 90 weight percent of the total coating composition.

The coating compositions of the present invention contain one or more of the reactive vinyl dye compounds described herein. The concentration of the dye compound or compounds may be from about 0.005 to 30.0, preferably from about 0.05 to 15.0, weight percent based on the weight of the polymerizable vinyl compound(s) present in the coating composition, i.e., component (i) of the coating compositions. The coating compositions of the present invention normally contain a photoinitiator. The amount of photoinitiator typically is about 1 to 15 weight percent, preferably about 3 to about 5 weight percent, based on the weight of the polymerizable vinyl compound(s) present in the coating composition. Typical photoinitiators include benzoin and benzoin ethers such as marketed under the tradenames ESACURE BO, EB1, EB3, and EB4 from Fratelli Lamberti; VICURE 10 and 30 from Stauffer; benzil ketals such as 2,2-dimethoxy-1,2-diphenylethan-1-one (IRGACURE 651), 2-hydroxy-2-methyl-1-phenylpropan-1-one (IRGACURE 1173), 2-methyl-2-morpholino-1-(p-methylthiophenyl)propan-1-one (IRGACURE 907), alpha-hydroxyalkyl-phenones such as (1-hydroxycyclohexyl)(phenyl)methanone (IRGACURE 184), 2-benzyl-2-(dimethylamino)-1-(4-morpholinophenyl)butan-1-one (IRGACURE 369), 2-hydroxy-2-methyl-1-phenylpropan-1-one IRGACURE 1173) from Ciba Geigy, Uvatone 8302 by Upjohn; alpha, alpha-dialkoxyacetophenone derivatives such as DEAP and UVATONE 8301 from Upjohn; DAROCUR 116, 1173, and 2959 by Merck; and mixtures of benzophenone and tertiary amines In pigmented coating compositions, the rate of cure can be improved by the addition of a variety of phosphine oxide photoinitiaters such as bis(2,4,6-trimethylbenzoyl)-phenylphosphine oxide (Irganox 819), Irgacure 819, 1700, and 1700 and phosphine oxide mixtures such as a 50/50 by weight mixtures of IRGACURE 1173 and 2,4,6-trimethylbenzoyidiphenylphosphine oxide (DAROCUR 4265) from Ciba. Further details regarding such photoinitiators and curing procedures may be found in the published literature such as U.S. Pat. No. 5,109,097, incorporated herein by reference. Depending upon the thickness of the coating (film), product formulation, photoinitiator type, radiation flux, and source of radiation, exposure times to ultraviolet radiation of about 0.5 second to about 30 minutes (50–5000 mJ/square cm) typically are required for curing. Curing also can occur from solar radiation, i.e., sunshine.

The coating compositions of the present invention may contain one or more additional components typically present in coating compositions. Examples of such additional components include leveling, rheology, and flow control agents such as silicones, fluorocarbons or cellulosics; flatting agents; pigment wetting and dispersing agents; surfactants; ultraviolet (UV) absorbers; UV light stabilizers; tinting pigments; defoaming and antifoaming agents; anti-settling, anti-sag and bodying agents; anti-skinning agents; anti-flooding and anti-floating agents; fungicides and mildewcides; corrosion inhibitors; thickening agents; and/or coalescing agents. The coating compositions of the present invention also may contain non-reactive modifying resins. Typical non-reactive modifying resins include homopolymers and copolymers of acrylic and methacrylic acid; homopolymers and copolymers of alkyl esters of acrylic and methacrylic acid such as methyl, ethyl, n-propyl, isopropyl, butyl, tetrahydrofurfuryl, cyclohexyl, isobornyl, n-hexyl, n-octyl, isooctyl, 2-ethylhexyl, lauryl, stearyl, and benzyl acrylate and methacrylate; acrylated and methacrylated urethane, epoxy, and polyester resins, silicone acrylates, cellulose esters such as cellulose acetate butyrates, cellulose acetate, propionates, nitrocellulose, cellulose ethers such as methyl cellulose, ethyl cellulose, hydroxypropyl cellulose, and hydroxypropyl methyl cellulose.

Typical plasticizers include alkyl esters of phthalic acid such as dimethyl phthalate, diethyl phthalate, dipropyl phthalate, dibutyl phthalate, and dioctyl phthalate; citrate esters such as triethyl citrate and tributyl citrate; triacetin and tripropionin; and glycerol monoesters such as Eastman 18-04, 18-07, 18-92 and 18-99 from Eastman Chemical Company. Specific examples of additional additives can be found in Raw Materials Index, published by the National Paint & Coatings Association, 1500 Rhode Island Avenue, N.W., Washington, D.C. 20005.

The ninth embodiment of the present invention pertains to a polymeric composition, typically a polymeric coating, comprising a polymer of one or more acrylic acid esters, one or more methacrylic acid esters and/or other polymerizable vinyl compounds, having copolymerized therein one or more of the dye compounds described above. The colored polymeric compositions provided by our invention may be prepared from the coating compositions described above and typically contain from about 0.005 to 30.0 weight percent, preferably from about 05 to 15.0 weight percent, of the reactive or polymerized residue of one or more of the vinyl dye compounds described herein based on the weight of the composition or coating. The novel polymeric coatings may have a thickness of about 2.5 to 150 microns, more typically about 15 to 65 microns.

The polymeric coatings of the present invention typically have a solvent resistance of at least 100 MEK double rubs using ASTM Procedure D-3732; preferably a solvent resistance of at least about 200 double rubs. Such coatings also typically have a pencil hardness of greater than or equal to F using ASTM Procedure D-3363; preferably a pencil hardness of greater than or equal to H. The coating compositions can be applied to substrates with conventional coating equipment. The coated substrates are then exposed to radiation such as ultraviolet light in air or in nitrogen which gives a cured finish. Mercury vapor or Xenon lamps are applicable for the curing process. The coatings of the present invention can also be cured by electron beam.

The radiation-curable coating compositions of this invention are suitable as adhesives and coatings for such substrates as metals such as aluminum and steel, plastics, glass, wood, paper, and leather. On wood substrates the coating compositions may provide both overall transparent color and grain definition. Various aesthetically-appealing effects can be achieved thereby. Due to reduced grain raising and higher film thicknesses, the number of necessary sanding steps in producing a finished wood coating may be reduced when using the colored coating compositions of the invention rather than conventional stains. Coating compositions within the scope of our invention may be applied to automotive base coats where they can provide various aesthetically-appealing effects in combination with the base coats and color differences dependent on viewing angle (lower angles create longer path lengths and thus higher observed color intensities). This may provide similar styling effects as currently are achieved with metal flake orientation in base coats.

Various additional pigments, plasticizers, and stabilizers may be incorporated to obtain certain desired characteristics in the finished products. These are included in the scope of the invention.

Coating, Curing, and Testing Procedures:

Samples of formulations were used to coat glass plates using a knife blade. The wet film thickness was about 15 to 75 microns (0.6 to 3.0 mils). The solvent was evaporated to give a clear, somewhat tacky film. Prior to exposure to UV radiation, each film was readily soluble in organic solvents.

The dried film on the glass plate was exposed to UV radiation from a 200 watt per inch medium pressure mercury vapor lamp housed in an American Ultraviolet Company instrument using a belt speed of 25 ft. per minute. One to five passes under the lamp resulted in a crosslinked coating with maximum hardness and solvent resistance.

Each cured coating (film) may be evaluated for Konig Pendulum Hardness (ASTM D4366 DIN 1522), solvent resistance by the methyl ethyl ketone double-rub test, and solubility in acetone before and after exposure to UV radiation. The damping time for Konig Pendulum Hardness on uncoated glass is 250 seconds; coatings with hardness above 100 seconds are generally considered hard coatings. The methyl ethyl ketone (MEK) double rub test is carried out in accordance with ASTM Procedure D-3732 by saturating a piece of cheese cloth with methyl ethyl ketone, and with moderate pressure, rubbing the coating back and forth. The number of double rubs is counted until the coating is removed. The acetone solubility test is carried out by immersing a dry, pre-weighed sample of the cured film in acetone for 48 hours at 25° C. The film is removed, dried for 16 hours at 60° C. in a forced-air oven, and reweighed. The weight percent of the insoluble film remaining is calculated from the data.

COATING EXAMPLES

The coatings and coating compositions provided by the present invention and the preparation thereof are further illustrated by the following examples.

Example 217

A colored, photopolymerizable composition was prepared by thoroughly mixing 0.5 g the yellow dye of Example 7 with a coating composition consisting of 20 g Jätgalux UV500 polyester acrylate, 10 g of bisphenol A epoxy acrylate, 9 g dipropyleneglycol diacrylate (DPGDA), 7 g trimethylolpropane triacrylate (TMPTA), and 4 g of Darocure 1173 photoinitiator using a small Cowles mixer until the components were completely dispersed. The resulting coating composition containing 1% of the yellow dye was drawn down with a wire wound rod to provide a 25.4 micron (1 mil) thick coating on an oak wood panel. This panel was passed through a UV cure machine at a speed of 6.1 meters per minute (20 feet/minute) using a lamp with an intensity of 118.1 watts per cm (300 watts per inch). The same coating solutions were applied to glass panels and cured under the same conditions of exposure. Konig Pendulum Hardness measurements (ASTM D4366 DIN 1522) were conducted on the coated glass panels and indicated no significant loss of hardness due to incorporation of the dye; hardness was 86 Konig seconds compared with 82 seconds for a reference coating, which contained no polymerizable dye. Adhesion of the coating to an oak wood panel was measured using the crosshatch adhesion method according to ASTM method D 3359 (ISO 2409). A right angle lattice pattern (6 lines in each direction) is cut into the coating, penetrating to the substrate, creating 25 squares with each side of the squares measuring 1 mm. A 2.5 cm (1 inch) wide piece of tape is applied to the lattice, pressure is applied, and then the tape is pulled from the substrate. If the edges are smooth and none of the squares are detached, the adhesion is 100% (ASTM rating 5B). On the wood panel a 5B rating was achieved for both the reference and the dye-containing coatings. Chemical resistance was tested with MEK double rubs on glass. Both the reference, which contained no polymerizable dye, and the coatings, which contained polymerizable dyes, withstood more than 300 MEK double rubs. No dye color was observed on the white cheesecloth of the MEK rub test, which is an indication that the dyes cannot be extracted from the coatings with solvents and demonstrates complete incorporation of the dye into the polymer matrix of the cured film.

Example 218

A colored, photopolymerizable composition was prepared by thoroughly mixing 0.5 g the red dye of Example 8b with a coating composition consisting of 20 g Jägalux UV1500 polyester acrylate, 10 g of bisphenol A epoxy acrylate, 9 g dipropyleneglycol diacrylate (DPGDA), 7 g trimethylolpropane triacrylate (TMPTA), and 4 g of Darocure 1173 photoinitiator in a small Cowles mixer until the components were completely dispersed. The resulting coating composition, which contained 1% of the red dye, was drawn down with a wire wound rod to provide a 25.4 micron (1 mil) thick coating on an oak wood panel. This panel was passed through a UV cure machine at a speed of 6.1 meters per minute (20 feet/minute) using a lamp with an intensity of 118.1 watts per cm (300 wafts per inch). The same coating solutions were applied to glass panels and cured under the same conditions of exposure. Konig Pendulum Hardness measurements conducted on the coated glass panels showed no significant loss of hardness due to incorporation of the dye; hardness was 76 Konig seconds compared with 82 seconds for a reference coating which contained no polymerizable dye.

The invention has been described in detail with particular reference to preferred embodiments thereof, but it will be understood that variations and modifications can be effected within the spirit and scope of the invention. 

1. Photopolymerizable colorant compounds having Formula I: A—(—CO₂—X)_(n)  I wherein A, is a mono-, di-, tri- or tetravalent anthrapyridone chromophore; X is —R₁—O-Q or the phtopolymerizable group —CH₂—C₆H₄-p-C(R₂)═CH₂; R₁ is C₂–C₈ alkylene, —(—CH₂CH₂O—)_(m)—CH₂CH₂- or 1,4-cyclohexylenedimethylene; R₂ is hydrogen or C₁–C₆ alkyl; n is 1 to 4; m is 1–3; Q is a photopolymerizable group selected from an organic radical having the formula: —COC(R₃)═CH—R₄  Ia —CONHCOC(R₃)═CH—R₄  IIa —CONH—C₁–C₆-alkylene OCOC(R₃)═CH—R₄  IIIa

—COCH═CH—CO₂R₇Va

wherein R₃ is hydrogen or C₁–C₆ alkyl; R₄ is hydrogen; C₁–C₆ alkyl; phenyl; phenyl substituted with one or more groups selected from C₁–C₆ alkyl, C₁–C₆ alkoxy, —N(C₁–C₆ alkyl)₂, nitro, cyano, C₂–C₆ alkoxycarbonyl, C₂–C₆ alkanoyloxy and halogen; 1- or 2-naphthyl; 1- or 2-naphthyl substituted with C₁–C₆ alkyl or C₁–C₆ alkoxy; 2- or 3-thienyl; 2- or 3-thienyl substituted with C₁–C₆ alkyl or halogen; 2- or 3-furyl; or 2- or 3-furyl substituted with C₁–C₆ alkyl; R₅ and R₆ are independently selected from hydrogen, C₁–C₆ alkyl, substituted C₁–C₆ alkyl; or aryl; or R₅ and R₆ may be combined to represent a —(—CH₂—)₃₋₅— radical; R₇ is hydrogen or C₁–C₆ alkyl, substituted C₁–C₆ alkyl, C₃–C₈ alkenyl, C₃–C₈ cycloalkyl or aryl; and R₈ is hydrogen, C₁–C₆ alkyl or aryl.
 2. Photopolymerizable colorant compounds according to claim 1 wherein X is —CH₂CH₂OQ, —CH₂CH(CH₃)OQ, —(CH₂CH₂O)_(1,2)—CH₂CH₂OQ, —CH₂C(CH₃)₂CH₂OQ, or —CH₂—C₆H₁₀—CH₂OQ.
 3. Photopolymerizable colorant compounds according to claim 1 wherein Q is —COCH═CH₂ or —COC(CH₃)═CH₂.
 4. Photopolymerizable colorant compounds according to claim 1 wherein X is —CH₂—C₆H₄-4—C(R₂)═CH₂ wherein R₂ is hydrogen or methyl; or —R₁—O-Q wherein R₁ is —(CH₂)₂₋₄—, —CH₂CH(CH₃)—, —CH₂C(CH₃)₂CH₂—, —(CH₂CH₂O—)_(1,2)CH₂CH₂—, —CH₂CH(OH)CH₂—, or CH₂—C₆H₁₀-4—CH₂—; and Q is —COC(R₃)═CH₂ R₃ is hydrogen or methyl; or —CONHC(CH₃)₂—C₆H₄-4—C(CH₃)═CH₂.
 5. Process for the preparation of the photopolymerizable colorants defined in claim 1 wherein X is a p-vinylbenzyl radical having the formula —CH₂—C₆H₄-p-C(R₂)═CH₂ which comprises reacting colored acidic compounds having the structure: A-(—CO₂—H)_(n) with a compound having the structure ClCH₂—C₆H₄-p-C(R₂)═CH₂ in the presence of base.
 6. Process for the preparation of the colored photopolymerizable compounds defined in claim 1 wherein X is —CH₂CH₂—O-Q or —CH₂CH(CH₃)—O-Q, which comprises the steps of: (a) reacting colored acidic compounds having the structures: A-(—CO₂—H)_(n) with at least about n molecular equivalents of ethylene or propylene carbonate for each molecular equivalent of acidic compounds to produce the 2-hydroxyalkyl derivatives of said acidic compounds; (b) reacting said colored 2-hydroxyalkyl derivatives with about n molecular equivalents of one or more acylating agents having the structures: ClCOC(R₃)═CH—R₄ or O[COC(R₃)═CH—R₄]₂,  Ib O═C═N—COC(R₃)═CH—R₄,  IIb O═C═N—C₁–C₆ alkylene OCOC(R₃)═CH—R₄,  IIIb


7. A photopolymerizable anthrapyridone colorant having the formula

wherein R₂₈ is hydrogen, 4—C₁–C₆ alkoxy, 4-arylthio, 4-aryloxy, 4—C₁–C₆ alkylthio, 4—C₁–C₆ alkylsulfonyl, 4-arylsulfonyl, and 4-halogen; R₃₀ is hydrogen, C₁–C₈ alkyl, substituted C₁–C₈ alkyl, or aryl; R₃₁ is hydrogen, cyano, C₁–C₆ alkoxy, C₁–C₆ alkylthio, halogen, C₁–C₆ alkylsulfonyl, arylsulfonyl, aryl, arylthio, heteroaryl, heteroarylthio, C₂–C₆ alkoxycarbonyl, or aroyl; L₄ is 6—NH—or 6—S—; and X is —CH₂—C₆H₄-4—C(R₂)═CH₂, wherein R₂ is hydrogen or methyl, or —R₁—O-Q, wherein R₁ is —(CH₂)₂₋₄—, —CH₂CH(CH₃)—, —CH₂C(CH₃)₂CH₂—, —(CH₂CH₂O—)₁₋₂CH₂CH₂—, —CH₂CH(OH)CH₂—, or CH₂—C₆H₁₀-4—CH₂—, and Q is —COC(R₃)═CH₂, wherein R₃ is hydrogen or methyl; or X is —CONHC(CH₃)₂—C₆H₄-4—C(CH₃)═CH₂.
 8. A photopolymerizable anthrapyridone colorant compound having the formula

wherein R₂₈ is hydrogen, 4—C₁–C₆ alkoxy, 4-arylthio, 4-heteroarylthio, 4-aryloxy, 4—C₁–C₆ alkylthio, 4—C₁–C₆ alkylsulfonyl, 4-arylsulfonyl, or 4-halogen; R₃₀ is hydrogen, C₁–C₈ alkyl, substituted C₁–C₈ alkyl, or aryl; R₃₁ is hydrogen, cyano, C₁–C₆ alkoxy, C₁–C₆ alkylthio, halogen, C₁–C₆ alkylsulfonyl, arylsulfonyl, aryl, arylthio, heteroaryl, heteroarylthio, C₂–C₆ alkoxycarbonyl, or aroyl; L₄ is 6—NH—or 6—S—; and X is —CH₂—C₆H₄-4—C(R₂)═CH₂, wherein R₂ is hydrogen or methyl, or —R₁—O-Q, wherein R₁ is —(CH₂)₂₋₄—, —CH₂CH(CH₃)—,—CH₂C(CH₃)₂CH₂, ——(CH₂CH₂O—) ₁₋₂CH_(CH) ₂—, —CH₂CH(OH)CH₂—, or CH₂—C₆H₁₀—4—CH₂—, and Q is —COC(R₃)═CH₂, wherein R₃ hydrogen or methyl, or X is—CONHC(CH₃)₂—C₆H₄—4—C(CH₃)═CH₂. 